THE EFFECTS OF MICROSTRUCTURE AND FRACTURE SURFACE-ROUGHNESS ON NEAR THRESHOLD FATIGUE CRACK-PROPAGATION CHARACTERISTICS OF A 2-PHASE CAST STAINLESS-STEEL

被引：20

作者：

MURAKAMI, RI

KIM, YH

FERGUSON, WG

机构：

[1] UNIV AUCKLAND,DEPT CHEM & MAT ENGN,AUCKLAND,NEW ZEALAND

[2] UNIV TOKUSHIMA,DEPT MECH ENGN,TOKUSHIMA 770,JAPAN

来源：

FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES | 1991年 / 14卷 / 07期

关键词：

D O I：

10.1111/j.1460-2695.1991.tb00702.x

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

In this study, the effects of stress ratio, microstructure and fracture surface roughness on the fatigue properties of a two-phase cast stainless steel were investigated. This behaviour was examined by means of the fracture mechanics approach and fractography. The fatigue crack growth rate decreased with decreasing stress ratio. The stress ratio markedly influenced the fatigue crack growth rate as DELTA-K approached the DELTA-K(th) value. The roughness of the fracture surface was greater in the as-cast material than in the heat-treated material. Analysis of the crack growth data using DELTA-K(eff) showed that the effect of R ratio could be explained but that the effect of microstructure on crack growth rate could not.

引用

页码：741 / 748

页数：8

共 5 条

[1]

Paris P.C., Bucci R.J., Wessel E.T., Clark W.G., Mager T.R., pp. 141-176, (1972)

[2]

Cooke R.J., Irving P.E., Booth G.S., Beevers C.J., The slow fatigue crack growth and threshold behaviour of medium carbon alloy steel in air and vacuum, Engng Fract. Mech., 7, pp. 69-77, (1975)

[3]

Park D.H., Fine M.E., Origin of crack closure in the near‐threshold fatigue crack propagation of Fe and Al‐3% Mg, Fatigue Crack Growth Threshold Concepts, pp. 145-161, (1984)

[4]

Murakami R., Kim Y.H., pp. 9-16, (1989)

[5]

Murakami R., Akizono K., Kusukawa K., Comparison of fatigue crack propagation under repeated impacts in stable and unstable stainless steels, Proc. Role of Fract. Mech. Modern Tech., pp. 549-560, (1986)

← 1 →