OXIDE FORMATION OF K38G SUPERALLOY AND ITS SPUTTERED MICROGRAINED COATING

被引：77

作者：

LOU, HY

WANG, FH

ZHU, SL

XIA, BJ

ZHANG, LX

机构：

来源：

SURFACE & COATINGS TECHNOLOGY | 1994年 / 63卷 / 02期

基金：

中国国家自然科学基金;

关键词：

D O I：

10.1016/S0257-8972(05)80014-3

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The oxide scales formed on the cast Ni-based alloy K38G and its sputtered, micrograined coating at 1000-degrees-C in air have been investigated by optical, electron probe microanalysis, scanning and transmission electron microscopy, and X-ray diffraction measurements. Complex oxide scales formed on the cast alloy composed of the outer layer of Cr2O3, TiO2 and NiCr2O4 and the inner layer of Al2O3 are prone to spallation. On the contrary, only a thin oxide layer of Al2O3 can be observed on the sputtered alloy, and it was very adherent. The formation of the Al2O3 layer and its excellent adhesion may be attributed to the microcrystalline grains of the sputtered material.

引用

页码：105 / 114

页数：10

共 24 条

[1] THE ROLE OF ALUMINUM AND TITANIUM ON THE OXIDATION PROCESS OF A NICKEL-BASE SUPERALLOY IN STEAM AT 800-DEGREES-C [J].

ABE, F ;

ARAKI, H ;

YOSHIDA, H ;

OKADA, M .

OXIDATION OF METALS, 1987, 27 (1-2) :21-36

[2] THE EFFECTS OF CR, AL, TI, MO, W, TA, AND CB ON THE CYCLIC OXIDATION BEHAVIOR OF CAST NI-BASE SUPERALLOYS AT 1100-DEGREES-C AND 1150-DEGREES-C [J].

BARRETT, CA ;

MINER, RV ;

HULL, DR .

OXIDATION OF METALS, 1983, 20 (5-6) :255-278

[3]

BASU SN, 1991, OXID MET, V35, P44

[4] OXIDATION PROTECTION OF ALLOY IN-738-LC BY PLASMA ASSISTED VAPOR-DEPOSITED SILICA COATING [J].

BENNETT, MJ ;

TUSON, AT ;

KNIGHTS, CF ;

AYRES, CF .

MATERIALS SCIENCE AND TECHNOLOGY, 1989, 5 (08) :841-852

[5] OXIDATION OF NI-BASE ALLOYS IN ATMOSPHERES WITH WIDELY VARYING OXYGEN PARTIAL PRESSURES [J].

CHRIST, HJ ;

BERCHTOLD, L ;

SOCKEL, HG .

OXIDATION OF METALS, 1986, 26 (1-2) :45-76

[6]

Felix P, 1972, DEPOSITION CORROSION, P331

[7]

GIGGINS CS, 1969, T METALL SOC AIME, V245, P2495

[8]

GIGGINS CS, 1969, T METALL SOC AIME, V245, P2509

[9] ON THE OXIDATION MECHANISM OF ALUMINA FORMERS [J].

JEDLINSKI, J ;

BORCHARDT, G .

OXIDATION OF METALS, 1991, 36 (3-4) :317-337

[10] CERAMICS DUCTILE AT LOW-TEMPERATURE [J].

KARCH, J ;

BIRRINGER, R ;

GLEITER, H .

NATURE, 1987, 330 (6148) :556-558

← 1 2 3 →