LOW-LOSS POLYMERIC OPTICAL WAVE-GUIDES WITH HIGH THERMAL-STABILITY

被引:43
作者
USUI, M
IMAMURA, S
SUGAWARA, S
HAYASHIDA, S
SATO, H
HIKITA, M
IZAWA, T
机构
[1] NTT Opto-electronics Laboratories, Tokai
关键词
OPTICAL POLYMERS; OPTICAL WAVE-GUIDES;
D O I
10.1049/el:19940677
中图分类号
TM [电工技术]; TN [电子技术、通信技术];
学科分类号
0808 ; 0809 ;
摘要
Singlemode polymeric optical waveguides are fabricated by using newly synthesised deuterated polysiloxane with high transparency and high thermal stability, The propagation loss of the waveguides is measured and found to be less than 0.1dB/cm at 1.31mum and less than 0.5dB/cm at 1.55mum. The propagation loss dependence on wavelength in the infra-red region of the waveguide remains unchanged after heating at 120-degrees-C for 10h.
引用
收藏
页码:958 / 959
页数:2
相关论文
共 6 条
[1]   LOW-LOSS CHANNEL WAVE-GUIDES IN POLYMERS [J].
BOOTH, BL .
JOURNAL OF LIGHTWAVE TECHNOLOGY, 1989, 7 (10) :1445-1453
[2]  
GOTO K, 1994, TECH DIG SERIES, V3, P137
[3]   RING RESONATOR COMPOSED OF LOW-LOSS POLYMER WAVE-GUIDES AT 1.3-MU-M [J].
HIDA, Y ;
IMAMURA, S ;
IZAWA, T .
ELECTRONICS LETTERS, 1992, 28 (14) :1314-1316
[4]   POLYMER CHANNEL WAVE-GUIDES WITH LOW-LOSS AT 1.3 MU-M [J].
IMAMURA, S ;
YOSHIMURA, R ;
IZAWA, T .
ELECTRONICS LETTERS, 1991, 27 (15) :1342-1343
[5]   LOW-LOSS, HEAT-RESISTANT OPTICAL WAVE-GUIDES USING NEW FLUORINATED POLYIMIDES [J].
MATSUURA, T ;
ANDO, S ;
SASAKI, S ;
YAMAMOTO, F .
ELECTRONICS LETTERS, 1993, 29 (03) :269-271
[6]   COUPLING RATIO CONTROL OF POLYMERIC WAVE-GUIDE COUPLERS BY BENDING [J].
YOSHIMURA, R ;
NAKAGOME, H ;
IMAMURA, S ;
IZAWA, T .
ELECTRONICS LETTERS, 1992, 28 (23) :2135-2136