THE ENERGETICS OF LA2-XAXNIO4-Y (A = BA, SR)

被引:29
作者
DICARLO, J [1 ]
MEHTA, A [1 ]
BANSCHICK, D [1 ]
NAVROTSKY, A [1 ]
机构
[1] PRINCETON UNIV,DEPT GEOL & GEOPHYS SCI,PRINCETON,NJ 08544
关键词
D O I
10.1006/jssc.1993.1091
中图分类号
O61 [无机化学];
学科分类号
070301 ; 081704 ;
摘要
The enthalpy of formation of the solid solution series La2-xAxNiO4-y (A = Ba, Sr; 0 ≤ x ≤ 0.7 and -0.18 ≤ y ≤ 0.04) has been measured using high-temperature reaction calorimetry. As barium or strontium is substituted for lanthanum, the enthalpy of formation from the oxides becomes more exothermic. The enthalpy of formation from the component oxides and the enthalpy of oxidation for the barium- and the strontium-doped material for a given value of x is the same within the experimental uncertainty. From the measurements of the enthalpy of oxidation for the oxygen interstitial regime (y < 0) and the oxygen vacancy regime (y > 0), the oxygen Frenkel energy for the lanthanum nickelates has been found to be 43 ± 20 kJ/(mole O). Based on the oxidation enthalpy measurements, we argue that the excess holes in lanthanum nickelate are predominantly in Ni 3d-type bands. © 1993 Academic Press, Inc.
引用
收藏
页码:186 / 192
页数:7
相关论文
共 12 条
[1]   POSSIBLE HIGH-TC SUPERCONDUCTIVITY IN THE BA-LA-CU-O SYSTEM [J].
BEDNORZ, JG ;
MULLER, KA .
ZEITSCHRIFT FUR PHYSIK B-CONDENSED MATTER, 1986, 64 (02) :189-193
[2]   SOLID OXIDE SOLUTIONS AS CATALYSTS - A COMPARISON WITH SUPPORTED PT [J].
CARBERRY, JJ ;
RAJADURAI, S ;
ALCOCK, CB ;
LI, B .
CATALYSIS LETTERS, 1990, 4 (01) :43-48
[3]   A THERMOCHEMICAL STUDY OF LA2-XAXCUO4-Y (A = BA, SR, CA, PB) [J].
DICARLO, J ;
BULARZIK, J ;
NAVROTSKY, A .
JOURNAL OF SOLID STATE CHEMISTRY, 1992, 96 (02) :381-389
[4]   CRYSTAL-CHEMISTRY AND SUPERCONDUCTIVITY OF THE COPPER OXIDES [J].
GOODENOUGH, JB ;
MANTHIRAM, A .
JOURNAL OF SOLID STATE CHEMISTRY, 1990, 88 (01) :115-139
[5]  
KROGER FA, 1956, SOLID STATE PHYS, V3, P307
[6]   STRUCTURE OF LA2CUO4 AND LASRVO4 [J].
LONGO, JM ;
RACCAH, PM .
JOURNAL OF SOLID STATE CHEMISTRY, 1973, 6 (04) :526-531
[7]   NATURE OF HOLE STATES IN CUPRATE SUPERCONDUCTORS [J].
MEHTA, A ;
DICARLO, J ;
NAVROTSKY, A .
JOURNAL OF SOLID STATE CHEMISTRY, 1992, 101 (01) :173-185
[8]   PROGRESS AND NEW DIRECTIONS IN HIGH-TEMPERATURE CALORIMETRY [J].
NAVROTSKY, A .
PHYSICS AND CHEMISTRY OF MINERALS, 1977, 2 (1-2) :89-104
[9]  
NITADORI T, 1989, CHEM MATER, V1, P216
[10]   DIRECT CALORIMETRIC DETERMINATION OF ENERGETICS OF OXYGEN IN YBA2CU3OX [J].
PARKS, ME ;
NAVROTSKY, A ;
MOCALA, K ;
TAKAYAMAMUROMACHI, E ;
JACOBSON, A ;
DAVIES, PK .
JOURNAL OF SOLID STATE CHEMISTRY, 1989, 79 (01) :53-62