FREQUENCY INTERACTIONS IN HIGH-TEMPERATURE FATIGUE CRACK-GROWTH IN SUPERALLOYS

被引:22
作者
GHONEM, H
ZHENG, D
机构
[1] Univ of Rhode Island, Kingston, RI
来源
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 1992年 / 23卷 / 11期
关键词
D O I
10.1007/BF02646124
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The influence of high frequency loading on the subsequent low frequency crack growth behavior in nickel-based alloy 718 in laboratory air environment at 923 K has been investigated through the use of a sequential high/low frequency load waveform. The parameters that have been examined include the crack growth rate, fracture surface morphology, and slip line density at and below the fracture surface. Results of this study indicate that prior application of high frequency loading results in reduction of the subsequent low frequency crack growth rate. An attempt is made to interpret this type of modification as being a result of the crack tip conditioning through the increase in the slip line density during the high frequency part of the loading cycle. Furthermore, by linking the type of selective oxide formed at the crack tip to the degree of deformation in the crack tip zone, a correlation has been made between the increase in the slip line density in the crack tip zone during the preceding high frequency loading and the increase of the crack resistance to environment degradation effects during the subsequent low frequency loading.
引用
收藏
页码:3067 / 3072
页数:6
相关论文
共 18 条
[1]  
Andre E., 1990, ECAI 90. Proceedings of the 9th European Conference on Artificial Intelligence, P25
[2]  
Barker J.F., 1989, SUPERALLOY, P269, DOI 10.7449/1989/Superalloys_1989_269_277
[3]  
CHANG KM, 1991, SUPERALLOYS 718 625, P447
[4]   PLASTIC ZONE SIZES IN FATIGUED SPECIMENS OF INCO-718 [J].
CLAVEL, M ;
FOURNIER, D ;
PINEAU, A .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1975, 6 (12) :2305-2307
[5]   FREQUENCY AND WAVE-FORM EFFECTS ON FATIGUE CRACK GROWTH-BEHAVIOR OF ALLOY 718 AT 298-K AND 823-K [J].
CLAVEL, M ;
PINEAU, A .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1978, 9 (04) :471-480
[6]  
Floreen S., 1979, FATIGUE ENG MATER, V2, P401
[7]   DEPTH OF INTERGRANULAR OXYGEN DIFFUSION DURING ENVIRONMENT-DEPENDENT FATIGUE CRACK-GROWTH IN ALLOY-718 [J].
GHONEM, H ;
ZHENG, D .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1992, 150 (02) :151-160
[8]  
GHONEM H, 1992, IN PRESS MATER SCI E
[9]  
GHONEM H, 1991, NOV ASME WINT ANN M
[10]  
GHONEM H, 1990, AFOSR890285 BOLL AFB