INFLUENCE OF THE METHOD OF ALUMINA MODIFICATION ON FORMATION OF LOW-TEMPERATURE SOLID-SOLUTIONS IN MAGNESIA ALUMINA SYSTEMS

被引:21
作者
KORYABKINA, NA [1 ]
ISMAGILOV, ZR [1 ]
SHKRABINA, RA [1 ]
MOROZ, EM [1 ]
USHAKOV, VA [1 ]
机构
[1] CATALYSIS INST, PROSP AKAD LAVRENTIEVA 5, NOVOSIBIRSK 630090, USSR
来源
APPLIED CATALYSIS | 1991年 / 72卷 / 01期
关键词
SOLID SOLUTIONS; MAGNESIA ALUMINA; CALCINATION; HEAT TREATMENT;
D O I
10.1016/0166-9834(91)85028-T
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
Formation of solid solutions in magnesia-alumina systems has been studied. It has been shown that depending on the method of introduction of magnesium and the temperature of heat treatment, formation of three types of solid solutions with the structure of gamma-alumina is possible; the anionic, the anionic-cationic and the cationic type. The mechanical strength of the obtained samples of spherical alumina depends on the method of modification; the strongest samples are produced if magnesium is added to aluminium hydroxide with subsequent calcination at 820 K.
引用
收藏
页码:63 / 69
页数:7
相关论文
共 11 条
[1]  
COLOSMAN EZ, 1972, KINET KATAL, V13, P1036
[2]  
DATTA RK, 1968, RUSTUM ROY AM MINERA, V53, P1456
[3]  
EFFROS MD, 1971, IZV AN BSSR KN, V4, P14
[4]  
IVANOVA AS, 1985, KINET KATAL, V26, P429
[5]  
KANALINA VS, 1983, CATALYSIS CATALYSTS, P127
[6]  
LANGE F, 1983, J AM CERAM SOC, V66, P50
[7]  
LIMAR TF, 1972, IAN SSSR NEORG MATER, V8, P500
[8]  
MOROZ EM, 1987, KINET KATAL, V28, P699
[9]   STUDY OF STRUCTURAL AND MECHANICAL-PROPERTIES OF GRANULATED ALUMINA SUPPORTS USING X-RAY MICROPROBES [J].
OVSYANNIKOVA, IA ;
GOLDENBERG, GI ;
KORAYABKINA, NA ;
SHKRABINA, RA ;
ISMAGILOV, ZR .
APPLIED CATALYSIS, 1989, 55 (01) :75-80
[10]   MULTICOMPONENT TOUGHENED CERAMIC MATERIALS OBTAINED BY REACTION SINTERING .1. ZRO2-AL2O3-SIO2-CAO SYSTEM [J].
PENA, P ;
MIRANZO, P ;
MOYA, JS ;
DEAZA, S .
JOURNAL OF MATERIALS SCIENCE, 1985, 20 (06) :2011-2022