SELECTED THERMOPLASTIC BEARING MATERIALS FOR USE AT ELEVATED-TEMPERATURES

被引：26

作者：

HAGER, AM ^{[1
]}

FRIEDRICH, K ^{[1
]}

JUNGHANS, R ^{[1
]}

机构：

[1] TECH UNIV CHEMNITZ,WISSENSCH BEREICH TRIBSTECH,O-9010 CHEMNITZ,GERMANY

来源：

WEAR | 1993年 / 162卷 / pt B期

关键词：

D O I：

10.1016/0043-1648(93)90062-Q

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

Various polyaryletherketone-based composites were investigated with regard to their high temperature dry-sliding behaviour. In the range between room temperature and 220-degrees-C, all grade with a polytetrafluoroethylene (PTFE) content of 10-15 wt.% exhibited a friction behaviour that is very similar to that of neat PTFE. Studies of the wear-pv relationship of some of the grades showed that fibre contents of 30 wt.% are found to stabilize the specific wear, up to pv products of 16 MPa m s-1.

引用

页码：649 / 655

页数：7

共 24 条

[1]

ARCHARD JF, 1958, WEAR, V2, P438

[2]

BARTHOLOMEYZIK W, 1990, TECH RUNDSCH, V33, P52

[3]

BENNINGHOFF H, 1986, TECH RUNDSCH, V47, P43

[4] WEAR CHARACTERISTICS OF COMPOSITES - EFFECT OF FIBER ORIENTATION [J].

CHANG, HW .

WEAR, 1983, 85 (01) :81-91

[5]

EVANS DC, 1978, I MECH E C PUBLICATI, P1

[6] EFFECTS OF STEEL COUNTERFACE ROUGHNESS AND TEMPERATURE ON THE FRICTION AND WEAR OF PE(E)K COMPOSITES UNDER DRY SLIDING CONDITIONS [J].

FRIEDRICH, K ;

KARGERKOCSIS, J ;

LU, Z .

WEAR, 1991, 148 (02) :235-247

[7]

GERSDORFER O, 1970, VDI BER, V141, P43

[8]

GOZDAWA RJ, 1989, TRIBOLOGICAL DESIGN, P345

[9]

HINTERMANN HE, 1972, SCHWEIZ ARCH, V38, P51

[10]

KUNZE K, 1985, PLASTE KAUTSCH, V32, P103

← 1 2 3 →