CRYSTALLIZATION OF POLY(VINYLIDENE FLUORIDE) - EQUILIBRIUM MELTING-POINT AND HEAT OF FUSION OF ALPHA-POLYMORPH

In the reported experiments, samples of poly(vinylidene fluoride) were crystallized either (a) isothermally at a series of temperatures, or (b) in the presence of varying amounts of diluent (dimethylphthalate or dimethylacetamide). The alpha -polymorph was the only crystalline form present in these samples. Melting points of the first series (a) were determined by DSC and of the second (b) by dilatometry. The same equilibrium melting point for the alpha -polymorph (178 degree C) was obtained from the analysis of the two sets of data. A value of 1425 cal mole** minus **1 (5. 96 kJ mole** minus **1) for the heat of fusion of this polymorph was obtained from analysis of the polymer-diluent melting data. The heat of fusion and the entropy of fusion calculated therefrom correlated well with corresponding values for other fluoroethylene polymers. The melting point for fluoropolymer predicted, 222 degree C, agreed remarkably well with that determined for an experimental sample, thereby lending support to the empirical correlations. The heat of fusion of poly(trifluoroethylene) is, therefore, expected to be approximately 1300 cal mole** minus **1.