STRAIN-ENERGY DENSITY APPROACH TO STABLE CRACK EXTENSION UNDER NET SECTION YIELDING OF AIRCRAFT FUSELAGE

被引：28

作者：

JEONG, DY ^{[1
]}

ORRINGER, O ^{[1
]}

SIH, GC ^{[1
]}

机构：

[1] LEHIGH UNIV,INST FRACTURE & SOLID MECH,BETHLEHEM,PA 18015

来源：

THEORETICAL AND APPLIED FRACTURE MECHANICS | 1995年 / 22卷 / 02期

关键词：

D O I：

10.1016/0167-8442(94)00053-4

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

In this paper, the incremental theory of plasticity is used in conjunction with the strain energy density criterion to determine the stress field in 4-in. wide test specimens containing 3 holes. These specimens, made from 0.04-in. thick sheets of 2024-T3 aluminum, also contained small collinear cracks emanating from the holes. The initial crack sizes varied from 0.15 to 0.26 in. Residual strength tests conducted with these specimens revealed that stable tearing occurred before failure. Analyses were performed to predict the stable crack extension and failure by plastic collapsed. Because of: the complexities involved with nonlinear stress analysis combined with subcritical crack extension, the finite element method was used with the grid pattern adjusted for each increment of stable tearing. Reasonable correlation between the experimental data and predicted results was achieved.

引用

页码：127 / 137

页数：11

共 14 条

[1]

CARPINTERI A, 1984, THEORETICAL APPLIED, V1, P149

[2]

Irwin GR., 1957, J APPL MECH, V24, P361, DOI [10.1115/1.4011547, DOI 10.1111/J.1460-2695.2012.01707.X]

[3]

JABLONSKI DA, 1993, DOTVNTSCFAA939 FIN R

[4]

JABLONSKI DA, 1993, DOTFAACT9376 FIN REP

[5]

MCCABE DE, 1973, ASTM STP, V527

[6] COLLAPSED CUBIC ISOPARAMETRIC ELEMENT AS A SINGULAR ELEMENT FOR CRACK PROBLEMS [J].

PU, SL ;

HUSSAIN, MA ;

LORENSEN, WE .

INTERNATIONAL JOURNAL FOR NUMERICAL METHODS IN ENGINEERING, 1978, 12 (11) :1727-1742

[7]

SAMAVEDAM G, 1994, DOTFAACT9410 FIN REP

[8]

SAMAVEDAM G, 1994, DOTVNTSCFAA938 FIN R

[9] FRACTURE INITIATION UNDER GROSS YIELDING - STRAIN-ENERGY DENSITY CRITERION [J].

SIH, GC ;

MADENCI, E .

ENGINEERING FRACTURE MECHANICS, 1983, 18 (03) :667-677

[10] CRACK-GROWTH RESISTANCE CHARACTERIZED BY THE STRAIN-ENERGY DENSITY-FUNCTION [J].

SIH, GC ;

MADENCI, E .

ENGINEERING FRACTURE MECHANICS, 1983, 18 (06) :1159-1171

← 1 2 →