CHARACTERIZATION AND DEGRADATION STUDIES OF SUSPENSION-POLYMERIZED POLY(VINYL CHLORIDE) .1. THERMAL-DEGRADATION

被引：9

作者：

CHIRINOSPADRON, AJ ^{[1
]}

VONSCHOETTLER, GA ^{[1
]}

机构：

[1] INTEVEP SA,CARACAS 1070 A,VENEZUELA

来源：

POLYMER DEGRADATION AND STABILITY | 1991年 / 33卷 / 02期

关键词：

D O I：

10.1016/0141-3910(91)90018-M

中图分类号：

O63 [高分子化学（高聚物）];

学科分类号：

070305 ; 080501 ; 081704 ;

摘要：

The degradation behaviour of three suspension type poly(vinyl chloride) (PVC) resins was examined using UV-visible and IR spectroscopies, viscometry and thermal analysis. Both thermal and thermo-oxidative degradation characteristics were studied. Characterization of the resins showed the presence of residues from additives added during the polymerization stage. Although the lowest molecular weight resin showed the highest thermal stability, the results indicate that the presence of polymerization residues has a more significant effect on the degradation behaviour of the samples under investigation. The results differ from published data, which attribute differences observed in the degradation behaviour of PVC samples to molecular defects.

引用

页码：213 / 227

页数：15

共 27 条

[1]

BRAUNDRUP J, 1975, POLYM HDB

[2]

Burgess R.H., 1982, MANUFACTURE PROCESSI

[3]

BUTTERS G, 1982, PARTICULATE NATURE P

[4] CHARACTERIZATION OF POLY(VINYLCHLORIDE) [J].

CARREGA, ME .

PURE AND APPLIED CHEMISTRY, 1977, 49 (05) :569-579

[5]

GERMAR H, 1983, MAKROMOL CHEM, V60, P106

[6] DEFECTS IN THE MOLECULAR-STRUCTURE OF POLYVINYLCHLORIDE AND THEIR RELATION TO THERMAL-STABILITY [J].

GUYOT, A .

PURE AND APPLIED CHEMISTRY, 1985, 57 (06) :833-844

[7]

Guyot A., 1985, J VINYL TECHNOL, V7, P92

[8]

HIERTBERG T, 1985, J VINYL TECHNOL, V7, P53

[9] INFRARED STUDIES OF CONFORMATIONAL CHANGES IN POLYVINYL CHLORIDE [J].

KRIMM, S ;

ENOMOTO, S .

JOURNAL OF POLYMER SCIENCE PART A-GENERAL PAPERS, 1964, 2 (2PA) :669-&

[10] INFRARED SPECTRA AND ASSIGNMENTS FOR POLYVINYL CHLORIDE AND DEUTERATED ANALOGS [J].

KRIMM, S ;

SHIPMAN, JJ ;

FOLT, VL ;

BERENS, AR .

JOURNAL OF POLYMER SCIENCE PART A-GENERAL PAPERS, 1963, 1 (08) :2621-&

← 1 2 3 →