SHAPING OF TITANIUM DIBORIDE BY INJECTION-MOLDING OF PRECURSOR MATERIALS

被引：6

作者：

EDIRISINGHE, MJ

MCCOLLUM, JI

机构：

[1] Department of Materials Technology, Brunel University, Uxbridge

来源：

CERAMICS INTERNATIONAL | 1993年 / 19卷 / 02期

关键词：

D O I：

10.1016/0272-8842(93)90083-4

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 [材料科学与工程]; 080502 [材料学];

摘要：

Several TiO2 and B2O3 mixtures have been subjected to carbothermic reduction to synthesise titanium boride (TiB2) under various conditions. The mixture and conditions that gave the best yield of TiB2 was compounded with an organic vehicle. The resulting formulation was successfully injection moulded to produce test bars. Specimens produced from these test bars were subjected to removal of the organic vehicle and the optimum carbothermic reduction conditions to produce TiB2 bars.

引用

页码：113 / 120

页数：8

共 36 条

[1]

AMSTEIN EH, 1958, Patent No. 804242

[2]

EFFECT OF OXYGEN CONTAMINATION ON DENSIFICATION OF TIB2 [J].

BAIK, S ;

BECHER, PF .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1987, 70 (08) :527-530

[3]

BAUMGARTNER HR, 1984, J AM CERAM SOC, V67, P207, DOI 10.1111/j.1151-2916.1984.tb19744.x

[4]

Castaing J., 1977, Boron and refractory borides, P390

[5]

Cobb PC, 1990, MATER DESIGN, V11, P156

[6]

DUBECK M, 1959, Patent No. 2906605

[7]

Edirisinghe M.J., 1986, INT J HIGH TECHNOL C, V2, P249, DOI DOI 10.1016/0267-3762(86)90020-2

[8]

Edirisinghe M.J., 1986, INT J HIGH TECHNOL C, V2, P1

[9]

Edirisinghe M. J., 1986, P BRIT CERAMIC SOC, V38, P67

[10]

EDIRISINGHE MJ, 1987, BRIT CERAM TRANS J, V86, P18

← 1 2 3 4 →