PREPARATION OF MAGNETIC MANOPARTICLES (GAMMA-FE2O3) IN THE SILICA MATRIX

Nanoparticles gamma-Fe2O3 were prepared in silica matrix by sol-gel process. Conventional acid hydrolysis and polycondensation of tetraethyl orthosilicate (TEOS) were used for the preparation of porous silica matrix. Iron(III) nitrate was homogeneously dissolved in the initial TEOS solution. After gelification and drying, the xerogel was heat treated on the air at different temperature between 700 - 900-degrees-C. The heating products were studied by high resolution TEM and magnetic measurements. Monocrystalline nanoparticles of gamma-Fe2O3 of size ranging between 50 - 100 angstrom were observed by HR TEM in the sample heated at 900-degrees-C. Room temperature magnetic measurements show a week ferrimagnetic component for samples heated until 880-degrees-C, but a ferrimagnetic behaviour is evident at 4 K The samples heated at higher temperature show ferrimagnetic behaviour at room temperature.