SHEAR BANDS AND MICROSTRUCTURE OF AL SINGLE-CRYSTALS DURING ROLLING

被引：30

作者：

MORII, K ^{[1
]}

NAKAYAMA, Y ^{[1
]}

机构：

[1] UNIV OSAKA PREFECTURE,COLL ENGN,SAKAI,OSAKA 591,JAPAN

来源：

SCRIPTA METALLURGICA | 1985年 / 19卷 / 02期

关键词：

ALUMINUM METALLOGRAPHY - Lattice Defects;

D O I：

10.1016/0036-9748(85)90179-6

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Shear band formation has been observed in (211) left bracket 1 OVER BAR 11 right bracket single crystals of high purity aluminum rolled at 77K. Lamellae of dislocation walls (or microbands) occurred in crystals nearly parallel to one of the active slip planes prior to shear banding. Such microstructures were not observed after rolling at room temperature. The development of microbands is correlated with reduction in dynamic recovery during deformation.

引用

页码：185 / 188

页数：4

共 11 条

[1] SHEAR BANDS IN DEFORMED METALS
HATHERLY, M
MALIN, AS
[J]. SCRIPTA METALLURGICA, 1984, 18 (05): : 449 - 454
[2] INTRODUCTION TO THE VIEWPOINT SET ON SHEAR BANDS
HUTCHINSON, JW
[J]. SCRIPTA METALLURGICA, 1984, 18 (05): : 421 - 422
[3] SLIP GEOMETRY IN PARTIALLY CONSTRAINED DEFORMATION
KOCKS, UF
CHANDRA, H
[J]. ACTA METALLURGICA, 1982, 30 (03): : 695 - 709
[4] FATIGUE-INDUCED SHEAR BANDS IN FERRITIC SINGLE-CRYSTALS
MAGNIN, T
FOURDEUX, A
DRIVER, JH
[J]. ACTA METALLURGICA, 1982, 30 (01): : 273 - 278
[5] MALIN A, 1981, Z METALLKD, V72, P310
[6] ROLLING DEFORMATION OF (211) [111] SINGLE-CRYSTALS OF ALPHA-BRASS
MORII, K
MERA, M
NAKAYAMA, Y
[J]. TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1977, 18 (01): : 7 - 16
[7] MORII K, 1981, T JAPAN I MET, V27, P857
[8] MORII K, UNPUB ACTA METALL
[9] TRANSMISSION ELECTRON-MICROSCOPY OF SHEAR BAND FORMATION IN ROLLED COPPER SINGLE-CRYSTALS
NAKAYAMA, Y
MORII, K
[J]. TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1982, 23 (07): : 422 - 431
[10] OSTERLE W, 1984, 7TH P INT C TEXT MAT, P123

← 1 2 →