MAGNETIC STUDIES OF FE-Y COMPOSITIONALLY MODULATED THIN-FILMS

Compositionally modulated thin films of Y/Fe have been studied by using SQUID magnetometry. Samples were grown by electron-beam evaporation onto Kapton substrates. In the low applied field regime, the samples show irreversible behavior when they are submitted to ZFC-FC magnetization processes, increasing the irreversibility zone as the thickness of the Fe layers increases. In the high applied magnetic field regime (H≥10 000 Oe), samples show ferromagnetic behavior. The temperature dependence of the saturation magnetization has been studied, and it was found that both spin-wave excitations and Stoner excitations occur at temperatures higher than 40 K, and a marked deviation from the T 3/2 law was noted below 30 K.