3-DIMENSIONAL CRACK CLOSURE BEHAVIOR

被引：30

作者：

DAWICKE, DS ^{[1
]}

GRANDT, AF ^{[1
]}

机构：

[1] NASA,LANGLEY RES CTR,HAMPTON,VA 23665

来源：

ENGINEERING FRACTURE MECHANICS | 1990年 / 36卷 / 01期

关键词：

D O I：

10.1016/0013-7944(90)90101-L

中图分类号：

O3 [力学];

学科分类号：

08 ; 0801 ;

摘要：

A crack closure measurement technique involving fatigue striations was used to produce a 3-dimensional crack opening load profile for 2024-T351 aluminum alloy. The crack opening load profile, determined through the specimen thickness, was compared with crack opening load measurements made with strain gages and displacement gages. The results of this study indicate that a significant 3-dimensional variation in crack closure behavior occurs in the alloy examined. An understanding of this phenomenon is important in understanding crack growth behavior, predicting crack shape changes, and interpreting "standard" crack closure measurement techniques. © 1990.

引用

页码：111 / 121

页数：11

共 15 条

[1]

CLERIVET A, 1988, ASTM STP, V982, P583

[2]

Elber W., 1970, Engineering Fracture Mechanics, V2, P37, DOI 10.1016/0013-7944(70)90028-7

[3]

ELBER W, 1968, THESIS U NSW AUSTRAL

[4]

Elber W., 1971, SIGNIFICANCE FATIGUE, V486, P230

[5] CLOSURE BEHAVIOR OF SURFACE CRACKS [J].

FLECK, NA ;

SMITH, IFC ;

SMITH, RA .

FATIGUE OF ENGINEERING MATERIALS AND STRUCTURES, 1983, 6 (03) :225-239

[6] VARIATION OF FATIGUE-CRACK-OPENING LOAD WITH MEASUREMENT LOCATION [J].

MACHA, DE ;

CORBLY, DM ;

JONES, JW .

EXPERIMENTAL MECHANICS, 1979, 19 (06) :207-213

[7]

Newman Jr J.C., 1981, ASTM SPEC TECH PUBL, V748, P53, DOI 10.1520/STP748-EB

[8]

PHILLIPS EP, 1988, COMMUNICATION

[9]

Pitoniak F. J., 1974, Engineering Fracture Mechanics, V6, P663, DOI 10.1016/0013-7944(74)90065-4

[10] FATIGUE CRACK CLOSURE OF CORNER CRACKS LOCATED AT HOLES LOADED IN TENSION OR BENDING [J].

RAY, SK ;

PEREZ, R ;

GRANDT, AF .

FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1987, 10 (03) :239-250

← 1 2 →