INFLUENCE OF PREPARATION PROCEDURE ON SOME PHYSICAL-PROPERTIES OF BICUVOX

被引:46
作者
KROK, F
BOGUSZ, W
KUREK, P
WASIUCIONEK, M
JAKUBOWSKI, W
DYGAS, J
机构
[1] Institute of Physics, Warsaw University of Technology, 02-525 Warszawa
来源
MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY | 1993年 / 21卷 / 01期
关键词
D O I
10.1016/0921-5107(93)90268-R
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The influence of preparation conditions on some physical properties of BICUVOX.10 (Bi2V0.90Cu0.10O5.35) is reported. Differential thermal and X-ray analyses indicate that synthesis of the compound can be accomplished at 610-degrees-C. The densification characteristics show that high density BICUJVOX ceramic can be obtained after several minutes of sintering at 800-degrees-C. The electrical conductivity was studied by a.c. impedance methods. Separation of the contributions of grain interiors and grain boundaries to the total resistance was possible at temperatures below around 350-degrees-C. The Arrhenius plots of the total conductivity consist of two straight line sections with a change in slope at around 500-degrees-C. The activation energy was about 0.48 eV at high temperatures for all the samples. Below around 500-degrees-C the activation energy was in the range from 0.62 to 0.72 eV depending on the preparation procedure. Lower values of activation energy and higher values of conductivity were obtained for well-sintered samples, which is related to the smaller contribution of the grain boundaries to the total electrical resistance of a sample.
引用
收藏
页码:70 / 76
页数:7
相关论文
共 5 条
  • [1] THE BIMEVOX SERIES - A NEW FAMILY OF HIGH PERFORMANCES OXIDE ION CONDUCTORS
    ABRAHAM, F
    BOIVIN, JC
    MAIRESSE, G
    NOWOGROCKI, G
    [J]. SOLID STATE IONICS, 1990, 40-1 (pt 2) : 934 - 937
  • [2] HABERKO K, 1983, SCI B U MINING METAL, V47
  • [3] ELECTROCHEMICAL CHARACTERIZATION OF BIMEVOX OXIDE-ION CONDUCTORS
    IHARADA, T
    HAMMOUCHE, A
    FOULETIER, J
    KLEITZ, M
    BOIVIN, JC
    MAIRESSE, G
    [J]. SOLID STATE IONICS, 1991, 48 (3-4) : 257 - 265
  • [4] REISELHUBER K, IN PRESS ELECTROCHIM
  • [5] Electrical and structural investigations on a new bismuth lead vanadium oxide solid electrolyte
    Vannier, R.N.
    Mairesse, G.
    Nowogrocki, G.
    Abraham, F.
    Boivin, J.C.
    [J]. Solid State Ionics, 1992, 53-56 (pt 2) : 713 - 722