COLLOIDAL PROCESSING FOR PREPARATION OF LAMINATED COMPOSITES OF MULLITE/WOVEN FABRICS OF SI-TI-C-O FIBERS

被引：4

作者：

HIRATA, Y

TAKESHIMA, K

机构：

[1] Department of Applied Chemistry and Chemical Engineering, Faculty of Engineering, Kagoshima University, Kagoshima, 890

来源：

MATERIALS LETTERS | 1993年 / 17卷 / 06期

关键词：

D O I：

10.1016/0167-577X(93)90129-L

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

A sol-gel-processed mullite powder and woven fabrics of Si-Ti-C-O fibers were formed into laminated composites (6 vol% woven fabrics). The green composites were hot-pressed to near full density at 1650 degrees C for 1 h at 39 MPa in a N-2 atmosphere. The strength and fracture toughness of the dense composites ( > 99% of theoretical density) were measured at room temperature. The fracture toughness for monolithic mullite (1.6 MPa m(1/2)) was increased to 3.9 MPa m(1/2) by the addition of the woven fabrics. On the other hand, there was no significant difference in the flexural strength between monolithic mullite and the composite.

引用

页码：374 / 378

页数：5

共 24 条

[1] MULLITE FOR STRUCTURAL, ELECTRONIC, AND OPTICAL APPLICATIONS [J].

AKSAY, IA ;

DABBS, DM ;

SARIKAYA, M .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1991, 74 (10) :2343-2358

[2]

BENDER BA, 1992, CERAM ENG SCI P, V13, P889

[3]

CERASANO J, 1988, J AM CERAM SOC, V71, P1062

[4]

CERASANO J, 1988, J AM CERAM SOC, V71, P250

[5] HIGH-TEMPERATURE MECHANICAL-PROPERTIES OF MULLITE UNDER COMPRESSION [J].

DOKKO, PC ;

PASK, JA ;

MAZDIYASNI, KS .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1977, 60 (3-4) :150-155

[6]

FOLSOM CA, 1992, CERAM ENG SCI P, V13, P469

[7] CALCULATION OF INTERACTION ENERGY AND PHASE-DIAGRAM FOR COLLOIDAL SYSTEMS [J].

HIRATA, Y ;

NAKAGAMA, S ;

ISHIHARA, Y .

NIPPON SERAMIKKUSU KYOKAI GAKUJUTSU RONBUNSHI-JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 1990, 98 (04) :316-321

[8] EFFECTS OF PARTICLE CLASSIFICATION ON COLLOIDAL PROCESSING OF MULLITE [J].

HIRATA, Y ;

TAKESHIMA, K .

MATERIALS LETTERS, 1993, 16 (04) :169-174

[9] COLLOIDAL PROCESSING FOR LAMINATED COMPOSITES OF MULLITE ALUMINA WOVEN FABRICS [J].

HIRATA, Y ;

TAKESHIMA, K .

MATERIALS LETTERS, 1993, 17 (3-4) :125-130

[10]

ISMAIL MGMU, 1987, J AM CERAM SOC, V70, pC7, DOI 10.1111/j.1151-2916.1987.tb04857.x

← 1 2 3 →