KINETICS AND DIFFUSION STUDIES IN BAAL2O4 FORMATION

被引:12
作者
ALI, MM
AGARWAL, SK
AGARWAL, S
HANDOO, SK
机构
关键词
D O I
10.1016/0008-8846(94)00116-G
中图分类号
TU [建筑科学];
学科分类号
0813 ;
摘要
The paper presents formation kinetics of monobarium aluminate, BaO.Al2O3, (BA) in the temperature range of 1100-1380 degrees C. Activation energy of its formation from barium and aluminium oxide is calculated to be 68.6 Kcal/mole. In the presence of MgO, its formation is accelerated and the activation energy of reaction is found to be 47.3 Kcal/mole. The activation free energies of the reaction were found to increase in the presence of MgO (1.5% by weight). Diffusion coefficients (D) of reactions have also been calculated and the temperature dependence obeys the relationship, D = 9.596 x 10(-4) (- 24,800/RT) cm(2) sec(-1) and D = 9.552 x 10(-4) (- 20,900/RT) cm(2) sec(-1) without and with MgO respectively.
引用
收藏
页码:86 / 90
页数:5
相关论文
共 10 条
[1]   KINETICS AND DIFFUSION STUDIES IN CA2 FORMATION [J].
ALI, MM ;
RAINA, SJ ;
SINGH, VK .
CEMENT AND CONCRETE RESEARCH, 1989, 19 (01) :47-52
[2]   Reactions in solid states at room temperature I Announcement the rate of reaction in endothermic conversions. [J].
Jander, W .
ZEITSCHRIFT FUR ANORGANISCHE UND ALLGEMEINE CHEMIE, 1927, 163 (1/2) :1-30
[3]  
KINGERY WD, 1967, INTRO CERAMICS, P223
[4]  
MACKENZIE KJD, 1978, BRIT CERAM TRANS J, V77, P88
[5]  
RAINA SJ, 1992, 9 ICCC NEW DELHI, V3, P245
[6]   EPITAXIAL GROWTH OF SPINEL BY REACTION IN THE SOLID STATE [J].
ROSSI, RC ;
FULRATH, RM .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1963, 46 (03) :145-149
[7]  
SINGH VK, 1983, T INDIAN CERAM SOC, V42, P145
[8]  
SINGH VK, 1980, T J BRIT CERAM SOC, V79, P112
[9]   Chemical reaction in powder form quantities of two types of cyrstal [J].
Tammann, G .
ZEITSCHRIFT FUR ANORGANISCHE UND ALLGEMEINE CHEMIE, 1925, 149 (1/3) :21-34
[10]   The heat tinting of metals. [J].
Tammann, G .
ZEITSCHRIFT FUR ANORGANISCHE UND ALLGEMEINE CHEMIE, 1920, 111 (01) :78-89