THE UNDERCOOLING ALUMINUM

被引:71
作者
MUELLER, BA [1 ]
PEREPEZKO, JH [1 ]
机构
[1] UNIV WISCONSIN,DEPT MET & MINING ENGN,MADISON,WI 53706
来源
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 1987年 / 18卷 / 06期
关键词
D O I
10.1007/BF02668565
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
An important parameter affecting microstructure development during solidification is the amount of undercooling prior to nucleation. The undercooling potential of aluminum has been assessed by thermal analysis measurements on powder dispersions of the liquid metal. A number of variables have been identified which influence the undercooling of powder Al samples including powder coating, powder size, melt cooling rate, and melt superheat. Surface analysis by Auger electron spectroscopy indicates that changing the medium in which the powders are produced is an effective method of altering the coating chemistry. Factorial design analysis has been employed to quantify the potential of processing variables to increase the undercooling level obtainable in aluminum. The factorial analysis indicates that control of the powder coating through changing the medium in which the powders are produced is most effective in decreasing the nucleation temperature. Additionally, the finest powders produced in the medium which induces the least catalytic coating, when cooled at high rates, T = 500 °C/s, from low superheats, T s = 710 °C, are found to achieve the deepest undercooling, ΔT = 175 °C. These studies provide the basis for further increases in undercooling and for future investigations into the solidification reactions which produce both stable and metastable structures in aluminum alloys. © 1991 The Minerals, Metals and Materials Society, and ASM International.
引用
收藏
页码:1143 / 1150
页数:8
相关论文
共 28 条
[1]   THE EFFECT OF RAPID SOLIDIFICATION VELOCITY ON THE MICROSTRUCTURE OF AG-CU ALLOYS [J].
BOETTINGER, WJ ;
SHECHTMAN, D ;
SCHAEFER, RJ ;
BIANCANIELLO, FS .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1984, 15 (01) :55-66
[2]   AN ANALYSIS OF THE MICROSTRUCTURE OF RAPIDLY SOLIDIFIED AL-8 WT PCT FE POWDER [J].
BOETTINGER, WJ ;
BENDERSKY, L ;
EARLY, JG .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1986, 17 (05) :781-790
[3]  
BOX GEP, 1978, STATISTICS EXPT
[4]  
BURDEN MH, 1970, J I MET, V98, P249
[5]  
COHEN M, 1980, RAPID SOLIDIFICATION, V2, P1
[6]  
DRAPER NR, 1981, APPLIED REGRESSION A
[7]   SOLID-LIQUID INTERFACE TENSION OF AL-SN, AL-IN AND AL-SN-IN SYSTEMS [J].
EUSTATHOPOULOS, N ;
COUDURIER, L ;
JOUD, JC ;
DESRE, P .
JOURNAL OF CRYSTAL GROWTH, 1976, 33 (01) :105-115
[8]  
HILDEMAN GJ, 1982, HIGH STRENGTH POWDER, P249
[9]  
HILDEMAN GJ, 1984, COMMUNICATION
[10]   NUCLEATION, UNDERCOOLING AND HOMOGENEOUS STRUCTURES IN RAPIDLY SOLIDIFIED POWDERS [J].
HIRTH, JP .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1978, 9 (03) :401-404