FRACTURE OF TITANIUM-HYDROGEN ALLOYS

被引:21
作者
BEEVERS, CJ
WARREN, MR
EDMONDS, DV
机构
[1] Department of Physical Metallurgy and Science of Materials, The University, Birmingham
来源
JOURNAL OF THE LESS-COMMON METALS | 1968年 / 14卷 / 04期
关键词
D O I
10.1016/0022-5088(68)90162-8
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
Tensile tests on coarse-grained (~0.3 mm) commercially-pure titanium containing 0, 30, 50, 85, 250 and 525 p.p.m. of hydrogen have been carried out. The tests were performed at -196 °, -78 °, 20 °, 150 ° and 300 °C at a strain rate of ~1.0 × 10-3 sec-1. The hydrogen embrittlement of the titanium, measured in terms of a reduction in both fracture stress and elongation to fracture, was enhanced by increasing hydrogen content and decreasing test temperature. This mechanical behaviour has been correlated to the influence of precipitate morphology and test temperature on the introduction of cracks into the titanium matrix by failure associated with the hydride precipitates. © 1968.
引用
收藏
页码:387 / &
相关论文
共 6 条
  • [1] BEEVERS CJ, 1965, T METALL SOC AIME, V233, P780
  • [2] COTTERILL P, 1961, PROG MATER SCI, V9, P241
  • [3] JAFFEE RI, 1956, T AM I MIN MET ENG, V206, P907
  • [4] JAFFEE RI, 1958, PROGR METAL PHYS, V7, P117
  • [5] Lenning G. A., 1954, J MET, V6, P367
  • [6] AN EXPERIMENTAL AND THERMODYNAMIC INVESTIGATION OF THE HYDROGEN-TITANIUM SYSTEM
    MCQUILLAN, AD
    [J]. PROCEEDINGS OF THE ROYAL SOCIETY OF LONDON SERIES A-MATHEMATICAL AND PHYSICAL SCIENCES, 1950, 204 (1078): : 309 - 323