GRAIN-SIZE EFFECTS IN HYDROGEN-ASSISTED CRACKING

被引:80
作者
LESSAR, JF
GERBERICH, WW
机构
[1] MEDTRONIC INC,MINNEAPOLIS,MN 55418
[2] UNIV MINNESOTA,DEPT CHEM ENGN & MAT SCI,MINNEAPOLIS,MN 55455
来源
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 1976年 / 7卷 / 07期
关键词
D O I
10.1007/BF02644060
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
引用
收藏
页码:953 / 960
页数:8
相关论文
共 39 条
[1]  
AULT RT, 1967, T ASM, V60, P79
[2]   HYDROGEN PERMEABILITY AND DELAYED FAILURE OF POLARIZED MARTENSTIC STEELS [J].
BARTH, CF ;
STEIGERW.EA ;
TROIANO, AR .
CORROSION, 1969, 25 (09) :353-&
[3]  
BARTH CF, 1970, METALL TRANS, V1, P3451
[4]  
BEACHEM CD, 1972, METALL TRANS, V3, P437
[5]  
Brown BF., 1971, THEORY STRESS CORROS, P186
[6]  
Brown BF, 1965, CORROS SCI, V5, P745, DOI [10.1016/S0010-938X(65)80002-6., DOI 10.1016/S0010-938X(65)80002-6]
[7]  
Brown BF, 1968, METALL REV, V13, P171
[8]  
Carter C. S., 1971, Engineering Fracture Mechanics, V3, P1, DOI 10.1016/0013-7944(71)90047-6
[9]   EFFECT OF SILICON ON STRESS CORROSION RESISTANCE OF LOW ALLOY HIGH STRENGTH STEELS [J].
CARTER, CS .
CORROSION, 1969, 25 (10) :423-&
[10]  
Dunegan H. L., 1971, Engineering Fracture Mechanics, V2, P387, DOI 10.1016/0013-7944(71)90021-X