VISCOPLASTIC FLOW AND SHEAR THICKENING IN CONCENTRATED DIBLOCK COPOLYMER SOLUTIONS

Concentrated (typically 6%) solutions of a polystyrene-polyisoprene diblock copolymer in low viscosity paraffinic solvents form a micelle system by precipitating the polystyrene blocks, whereas the polyisoprene blocks are in solution. Besides viscoplastic behavior without thixotropy, this system exhibits a pronounced shear thickening in steady-state shear how. The micelles are stable up to shear rates of more than 10(5) s(-1). The properties of the solutions, especially the shear-thickening behavior, depend on the thermal history of the samples as well as on the solvent properties and are sensitive to flow field disturbances occurring in rotational viscometer devices with a profiled surface structure as commonly used to avoid wall slip in dispersed materials. The shear thickening is found to be related to the formation of a long-range ordered structure which also gives rise to the yield point. This long-range order enables aggregate flow with less energy dissipation at low shear rates. Shear-induced break-up of the aggregates appears as a shear-thickening transition which is observed in different types of flow fields.