CORDUROY CONTRAST IN TYPE-316 L STAINLESS-STEEL AFTER CYCLIC PLASTIC-DEFORMATION

被引：10
作者：
GERLAND, M
SAADI, BA
VIOLAN, P
机构：
[1] CNRS, Poitiers, Fr, CNRS, Poitiers, Fr
来源：
MATERIALS SCIENCE AND ENGINEERING | 1987年 / 96卷
关键词：
FAILURE ANALYSIS - IRON AND STEEL METALLOGRAPHY - Microstructures - STEEL - Hardening - STEEL TESTING - Fatigue - STRAIN - Analysis;
D O I：
10.1016/0025-5416(87)90584-2
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Samples of type 316 L stainless steel were fatigued at 300 degree C in vacuum at constant plastic strain amplitudes. An important secondary cyclic hardening occurred, mainly beyond the number of cycles corresponding to failure in air, which has been related to a particular microstructure similar to corduroy contrast observed on irradiated materials.
引用
收藏
页码：L1 / L4
页数：4
相关论文
共 12 条
[1]  
Adamson R. B., 1974, ASTM STP, V551, P215
[2]   CORDUROY CONTRAST OBSERVATIONS IN NEUTRON-IRRADIATED ZIRCONIUM AND ZIRCALOY [J].
BELL, WL .
JOURNAL OF NUCLEAR MATERIALS, 1975, 55 (01) :14-22
[3]  
BRAGER HR, 1971, METALL TRANS, V2, P1893
[4]   CREEP UNDER IRRADIATION OF 316 STEEL IN THE HIGH-VOLTAGE ELECTRON-MICROSCOPE [J].
CAILLARD, D ;
MARTIN, JL ;
JOUFFREY, B .
ACTA METALLURGICA, 1980, 28 (08) :1059-1067
[5]  
CAILLARD D, 1981, J MICROSC SPECT ELEC, V6, P361
[6]  
CAILLARD D, 1981, ANN CHIM-SCI MAT, V6, P37
[7]   SECONDARY CYCLIC HARDENING AND DISLOCATION-STRUCTURES IN TYPE-316 STAINLESS-STEEL AT 600-DEGREES-C [J].
GERLAND, M ;
VIOLAN, P .
MATERIALS SCIENCE AND ENGINEERING, 1986, 84 (1-2) :23-33
[8]   INTERPRETATION OF CORDUROY CONTRAST IN NEUTRON-IRRADIATED ZIRCONIUM [J].
KELLY, PM ;
BLAKE, RG ;
JOSTSONS, A .
JOURNAL OF NUCLEAR MATERIALS, 1976, 59 (03) :307-315
[9]   IRRADIATION DAMAGE IN ZIRCALOY-2 PRODUCED BY HIGH-DOSE ION-BOMBARDMENT [J].
LEE, D ;
KOCH, EF ;
ROSOLOWS.JH .
JOURNAL OF NUCLEAR MATERIALS, 1974, 50 (02) :162-174
[10]   DAMAGE ALIGNMENT IN NEUTRON-IRRADIATED ZIRCONIUM ALLOYS [J].
NORTHWOOD, DO ;
GILBERT, RW .
JOURNAL OF NUCLEAR MATERIALS, 1974, 51 (02) :271-276
12