CHANGES IN PHYSICAL AND MECHANICAL-PROPERTIES OF CARBON FIBER-REINFORCED POLYFURFURYL ALCOHOL COMPOSITES DURING THEIR PYROLYSIS TO CARBON-CARBON COMPOSITES

被引:26
作者
MANOCHA, LM
机构
[1] Natl Physical Lab, New Delhi, India, Natl Physical Lab, New Delhi, India
来源
COMPOSITES | 1988年 / 19卷 / 04期
关键词
CARBON FIBER - Mechanical Properties;
D O I
10.1016/0010-4361(88)90008-0
中图分类号
TB33 [复合材料];
学科分类号
摘要
Carbon/carbon composites were made by pyrolysis of polymer composites composed of polyfurfuryl alcohol resin and different surface treated high modulus carbon fibers. Shrinkage during pyrolysis was found to be dependent on the fiber/matrix bonding in polymer composites, being maximum for strongly bonded composites with surface treated fibers. Surface finish on carbon fibers was also found to have an effect on the carbonization shrinkage of the composites.
引用
收藏
页码:311 / 319
页数:9
相关论文
共 13 条
[1]  
BOYNE L, 1974, 4TH P LOND INT C CAR, P215
[2]  
Bradshaw W, 1978, CERAMIC B, V57, P193
[3]   INFLUENCE OF PROCESS PARAMETERS ON THE MECHANICAL-PROPERTIES OF CARBON-CARBON-COMPOSITES WITH PITCH AS MATRIX PRECURSOR [J].
FITZER, E ;
HUTTNER, W ;
MANOCHA, LM .
CARBON, 1980, 18 (04) :291-295
[4]   THE INFLUENCE OF CARBON-FIBER SURFACE-TREATMENT ON THE MECHANICAL-PROPERTIES OF CARBON-CARBON COMPOSITES [J].
FITZER, E ;
GEIGL, KH ;
HUTTNER, W .
CARBON, 1980, 18 (04) :265-270
[5]   THE FUTURE OF CARBON-CARBON COMPOSITES [J].
FITZER, E .
CARBON, 1987, 25 (02) :163-190
[6]  
GRAYSON M, 1983, ENCY COMPOSITE MATER, P10
[7]  
JENKINS GM, 1978, POLYM CARBONS
[8]  
KOTLENSKY WV, 1977, SAMPE Q APR, P1
[9]   EFFECT OF CARBON-FIBER SURFACE-TREATMENT ON MECHANICAL-PROPERTIES OF C/C COMPOSITES [J].
MANOCHA, LM ;
YASUDA, E ;
TANABE, Y ;
KIMURA, S .
CARBON, 1988, 26 (03) :333-337
[10]   INFLUENCE OF CARBON-FIBER TYPE AND WEAVE PATTERN ON THE DEVELOPMENT OF 2D CARBON CARBON COMPOSITES [J].
MANOCHA, LM ;
BAHL, OP .
CARBON, 1988, 26 (01) :13-21