PREPARATION AND CHARACTERIZATION OF CHROMIUM-OXIDE SUPPORTED ON ZIRCONIA

被引:26
作者
SOHN, JR [1 ]
RYU, SG [1 ]
PARK, MY [1 ]
PAE, YI [1 ]
机构
[1] ULSAN UNIV,NATL SCI COLL,DEPT CHEM,ULSAN 680749,SOUTH KOREA
关键词
D O I
10.1007/BF00414254
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Chromium oxide/zirconia was prepared by dry impregnation of powdered Zr(OH), with an aqueous solution of (NH4)2CrO4. The characterization of prepared samples was performed using Fourier-transform infrared (FTIR) spectroscopy, X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), and differential thermal analysis (DTA), and by measurement of the surface area. The addition of chromium oxide to zirconia shifted the transitions of ZrO2 from the amorphous to the tetragonal phase and from the tetragonal to the monoclinic phase to higher temperatures due to the strong interaction between chromium oxide and zirconia; and the specific surface area of the samples increased in proportion to the chromium-oxide content. Since the ZrO2 Stabilizes supported chromium oxide, chromium oxide was well dispersed on the surface of zirconia, and alpha-Cr2O3 was only observed at calcination temperatures above 1173 K. Upon the addition of only small amounts of chromium oxide (1 wt % Cr) to ZrO2, both the acidity and acid strength of the samples increased remarkably, showing the presence of two kinds of acid sites on the surface of CrOx/ZrO2 (Bronsted and Lewis acid sites).
引用
收藏
页码:4651 / 4659
页数:9
相关论文
共 35 条
[1]  
[Anonymous], [No title captured]
[2]   CHARACTERIZATION OF CROX-SIO2 CATALYSTS BY PHOTOELECTRON-SPECTROSCOPY (XPS), X-RAY AND OPTICAL MEASUREMENTS [J].
CIMINO, A ;
DEANGELIS, BA ;
LUCHETTI, A ;
MINELLI, G .
JOURNAL OF CATALYSIS, 1976, 45 (03) :316-325
[3]   THE NATURE OF SURFACE CHROMIUM SPECIES ON CROX/ZRO2 CATALYSTS [J].
CIMINO, A ;
CORDISCHI, D ;
FEBBRARO, S ;
GAZZOLI, D ;
INDOVINA, V ;
OCCHIUZZI, M ;
VALIGI, M ;
BOCCUZZI, F ;
CHIORINO, A ;
GHIOTTI, G .
JOURNAL OF MOLECULAR CATALYSIS, 1989, 55 (1-3) :23-33
[4]  
CLARK A, 1969, CATALY REV, V3, P145
[5]   CRYSTALLINE HYDROUS ZIRCONIA [J].
CLEARFIELD, A .
INORGANIC CHEMISTRY, 1964, 3 (01) :146-&
[6]   THE GENERATION OF BRONSTED AND LEWIS ACID SITES ON THE SURFACE OF SILICA BY ADDITION OF DOPANT CATIONS [J].
CONNELL, G ;
DUMESIC, JA .
JOURNAL OF CATALYSIS, 1987, 105 (02) :285-298
[7]   CATALYTIC CONVERSION OF ALCOHOLS .11. INFLUENCE OF PREPARATION AND PRETREATMENT ON THE SELECTIVITY OF ZIRCONIA [J].
DAVIS, BH ;
GANESAN, P .
INDUSTRIAL & ENGINEERING CHEMISTRY PRODUCT RESEARCH AND DEVELOPMENT, 1979, 18 (03) :191-198
[8]  
DZISKO VA, 1964, 3 P INT C CAT AMST, V1
[9]   IR INVESTIGATION OF POLYMERIZATION CENTERS OF THE PHILLIPS CATALYST [J].
GHIOTTI, G ;
GARRONE, E ;
ZECCHINA, A .
JOURNAL OF MOLECULAR CATALYSIS, 1988, 46 (1-3) :61-77
[10]   XPS STUDY OF THE SURFACE CARBONATION HYDROXYLATION STATE OF METAL-OXIDES [J].
GONZALEZELIPE, AR ;
ESPINOS, JP ;
FERNANDEZ, A ;
MUNUERA, G .
APPLIED SURFACE SCIENCE, 1990, 45 (02) :103-108