SUBSTRUCTURE OF THIN FOIL (225) FERROUS MARTENSITES

被引：8

作者：

OSHIMA, R ^{[1
]}

WAYMAN, CM ^{[1
]}

机构：

[1] UNIV ILLINOIS, DEPT MET & MIN ENGN, URBANA, IL 61801 USA

来源：

TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS | 1975年 / 16卷 / 02期

关键词：

D O I：

10.2320/matertrans1960.16.73

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

The substructure of thin foil martensite formed below room temperature was studied in Fe-6Mn-1C, Fe-5. 5Mn-1C, Fe-3Mn-3Cr-1C, and Fe-8Cr-1C steels using transmission electron microscopy and diffraction. As in bulk material, the martensite habit plane in the above alloys was found to be near left brace 225 right brace . Even though constraints are expected to be relaxed for thin foils (two-dimensional transformations), the observed substructure was found to be highy complex. This is described in detail.

引用

页码：73 / 86

页数：14

共 28 条

[1] THE CRYSTALLOGRAPHY OF MARTENSITE TRANSFORMATIONS .3. FACE-CENTRED CUBIC TO BODY-CENTRED TETRAGONAL TRANSFORMATIONS [J].

BOWLES, JS ;

MACKENZIE, JK .

ACTA METALLURGICA, 1954, 2 (02) :224-234

[2]

BOWLES JS, 1954, ACTA METALL MATER, V2, P129, DOI 10.1016/0001-6160(54)90102-9

[3] CONTINUOUS DISTRIBUTIONS OF DISLOCATIONS - SURFACE DISLOCATIONS AND THE CRYSTALLOGRAPHY OF MARTENSITIC TRANSFORMATIONS [J].

BULLOUGH, R ;

BILBY, BA .

PROCEEDINGS OF THE PHYSICAL SOCIETY OF LONDON SECTION B, 1956, 69 (12) :1276-1286

[4] DIRECT OBSERVATIONS OF PRETRANSFORMATION LATTICE INSTABILITIES [J].

CORNELIS, I ;

OSHIMA, R ;

TONG, HC ;

WAYMAN, CM .

SCRIPTA METALLURGICA, 1974, 8 (02) :133-143

[5] THE CRYSTALLOGRAPHY OF THE MARTENSITE REACTION IN STEEL [J].

CROCKER, AG ;

BILBY, BA .

ACTA METALLURGICA, 1961, 9 (07) :678-688

[6] CRYSTALLOGRAPHY OF FERROUS MARTENSITES [J].

DUNNE, DP ;

WAYMAN, CM .

METALLURGICAL TRANSACTIONS, 1971, 2 (09) :2327-&

[7]

Izotov VI, 1968, FIZ MET METALLOVED, V25, P98

[8]

JANA S, 1970, METALL TRANS, V1, P2825

[9] MARTENSITE TRANSFORMATION IN STEELS WITH LOW STACKING FAULT ENERGY [J].

KELLY, PM .

ACTA METALLURGICA, 1965, 13 (06) :635-&

[10] ON THEORY OF 225 MARTENSITE IN STEELS [J].

LIEBERMAN, DS ;

BULLOUGH, R .

PHYSICA STATUS SOLIDI, 1965, 12 (02) :657-+

← 1 2 3 →