FRACTURE-BEHAVIOR OF TOUGHENED EPOXY-RESINS CURED WITH N,N'-DIMETHYLETHYLENEDIAMINE

被引：5

作者：

MURAKAMI, S ^{[1
]}

WATANABE, O ^{[1
]}

INOUE, H ^{[1
]}

OCHI, M ^{[1
]}

SHIRAISHI, T ^{[1
]}

SHIMBO, M ^{[1
]}

机构：

[1] KANSAI UNIV,FAC ENGN,DEPT APPL CHEM,SUITA,OSAKA 564,JAPAN

来源：

POLYMER | 1992年 / 33卷 / 03期

关键词：

EPOXY RESINS; FRACTURE; CURING;

D O I：

10.1016/0032-3861(92)90734-E

中图分类号：

O63 [高分子化学（高聚物）];

学科分类号：

070305 ; 080501 ; 081704 ;

摘要：

Two series of toughened epoxy resin systems, which are models of matrix resins for use in carbon fibre reinforced plastics, were prepared. Evaluations of the cured epoxy resins, measuring fracture toughness, impact properties, tensile properties and dynamic mechanical properties were conducted. The correlations between these properties and the apparent concentration of network chains in the resins, nu, were investigated and the fracture surfaces were examined with a scanning electron microscope. The superior toughness of these resin systems was obtained without considerable loss in modulus. Unified maximum peak was observed in the plots of Izod impact strength, where the nu value of the cured resins was increased.

引用

页码：572 / 576

页数：5

共 15 条

[1]

BASCOM WD, 1981, J MATER SCI, V16, P2657, DOI 10.1007/BF02402827

[2]

BIAMANT J, 1984, 29TH P NAT SAMPE S, P422

[3]

DOUGLASS SK, 1981, J MATER SCI, V16, P3141

[4]

Douglass SK, 1980, J MATER SCI, V15, P1109

[5]

KATZ D, 1964, J POLYM SCI A2, P1595

[6]

KINLOCH AJ, 1987, POLYM COMMUN, V28, P322

[7] DEFORMATION AND FRACTURE-BEHAVIOR OF A RUBBER-TOUGHENED EPOXY .1. MICROSTRUCTURE AND FRACTURE STUDIES [J].

KINLOCH, AJ ;

SHAW, SJ ;

TOD, DA ;

HUNSTON, DL .

POLYMER, 1983, 24 (10) :1341-1354

[8] RUBBER-MODIFIED EPOXIES .2. MORPHOLOGY AND MECHANICAL-PROPERTIES [J].

MANZIONE, LT ;

GILLHAM, JK ;

MCPHERSON, CA .

JOURNAL OF APPLIED POLYMER SCIENCE, 1981, 26 (03) :907-919

[9] FRACTURE AND MECHANICAL-PROPERTIES OF EPOXY-RESINS AND RUBBER-MODIFIED EPOXY-RESINS [J].

MEEKS, AC .

POLYMER, 1974, 15 (10) :675-681

[10]

Murakami A., 1985, Journal of the Society of Materials Science, Japan, V34, P1099, DOI 10.2472/jsms.34.1099

← 1 2 →