INVESTIGATION OF THE PLASTICITY OF INP AS A FUNCTION OF TEMPERATURE

被引：5

作者：

LEBOURHIS, E

ZOZIME, A

RIVIERE, A

VERMEULIN, C

机构：

来源：

JOURNAL DE PHYSIQUE III | 1995年 / 5卷 / 11期

关键词：

D O I：

10.1051/jp3:1995226

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Compression tests at constant strain rate were performed on [ 001 ] oriented single crystals of undoped indium phosphide, in the temperature range 300 degrees C (0.43 Tm) to 700 degrees C (0.72 Tm). Critical resolved shear stresses are compared with those reported in the literature. Scanning electron microscopy in the cathodoluminescence mode and transmission electron microscopy were used to investigate the deformed sample microstructure. No microtwinning was observed.

引用

收藏

页码：1795 / 1801

页数：7

相关论文

共 14 条

[1] PLASTIC-DEFORMATION, EXTENDED STACKING-FAULTS AND DEFORMATION TWINNING IN SINGLE-CRYSTALLINE INDIUM-PHOSPHIDE .1. UNDOPED INP [J].

AZZAZ, M ;

MICHEL, JP ;

GEORGE, A .

PHILOSOPHICAL MAGAZINE A-PHYSICS OF CONDENSED MATTER STRUCTURE DEFECTS AND MECHANICAL PROPERTIES, 1994, 69 (05) :903-924

[2] ON THE FORMATION OF EXTENDED STACKING-FAULTS WITH EXTRINSIC CHARACTER IN DEFORMED INDIUM-PHOSPHIDE [J].

AZZAZ, M ;

MICHEL, JP ;

JACQUES, A ;

GEORGE, A .

PHYSICA STATUS SOLIDI A-APPLIED RESEARCH, 1993, 137 (02) :401-410

[3]

AZZAZ M, 1991, THESIS I NATIONAL PO

[4]

BRETHEAU T, 1979, ADV PHYS, V28, P829, DOI 10.1080/00018737900101455

[5] DEFORMATION-BEHAVIOR OF SINGLE-CRYSTALS OF INP IN UNIAXIAL COMPRESSION [J].

BROWN, GT ;

COCKAYNE, B ;

MACEWAN, WR .

JOURNAL OF MATERIALS SCIENCE, 1980, 15 (06) :1469-1477

[6] HIGH-TEMPERATURE MECHANICAL-PROPERTIES OF GAAS SINGLE-CRYSTALS - EFFECT OF INDIUM DOPING AND OF ENVIRONMENT [J].

DJEMEL, A ;

CASTAING, J .

EUROPHYSICS LETTERS, 1986, 2 (08) :611-615

[7] THERMAL-ACTIVATION OF DEFORMATION IN S-DOPED INP SINGLE-CRYSTALS [J].

GALL, P ;

PEYRADE, JP ;

COQUILLE, R ;

REYNAUD, F .

JOURNAL OF CRYSTAL GROWTH, 1987, 82 (04) :689-694

[8]

LEBOURHIS E, 1994, 13 ICEM A, V2, P13

[9]

LEBOURHIS E, 1994, THESIS U PARIS 7

[10]

LUYSBERG M, 1994, 13 ICEM A, V2, P11