CRYSTAL-TO-AMORPHOUS TRANSFORMATION OF NITI INDUCED BY COLD-ROLLING

A NiTi intermetallic compound was cold rolled at room temperature by 30% and 60% thickness reductions, and microstructures were studied by means of transmission electron microscopy (TEM). In the cold-rolled samples we observed both a phase of nanometer-sized crystals and an amorphous phase. A substantially high dislocation density, 1013 to 1014/cm2, was evident in the transition region between crystalline and amorphous phases. A simple estimate of the elastic energy arising from this dislocation density is of the same order as the crystallization energy, suggesting that dislocation accumulation is a major driving force for amorphization in cold-rolled NiTi. © 1990, Materials Research Society. All rights reserved.