PSEUDO-BINARY PB(MG1/3NB2/3)O3-PBO PHASE-DIAGRAM AND CRYSTAL-GROWTH OF PB(MG1/3NB2/3)O3 [PMN]

被引:74
作者
YE, ZG
TISSOT, P
SCHMID, H
机构
[1] Département de chimie minérale, analytique et appliquée, Université de Genève
关键词
D O I
10.1016/0025-5408(90)90202-D
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
A pseudo-binary phase diagram between the perovskite Pb(Mg 1 3Nb 2 3)O3 and PbO has been established by D.T.A.. The melting point of PMN was found at 1320°C and the eutectic temperature at 830±2°C with the eutectic composition of 74%PbO 26%PMN (in wt%). On the basis of the determined phase diagram single crystals of the perovskite phase have been grown by the high temperature solution technique by using 30wt% PbO as solvent. The obtained crystals show pseudo-cubic form with (100)cub. growth steps or degenerated forms. Size (∼ 1cm) and quality of the obtained crystals are adequate for physical characterizations. © 1990.
引用
收藏
页码:739 / 748
页数:10
相关论文
共 45 条
[1]  
AFANASEV II, 1977, OPT-MEKH PROMST, V44, P40
[2]  
ANDREEV EM, 1983, ROST KRISTALLOV ZHID, P79
[3]  
ARNDT H, 1988, FERROELECTRICS, V79, P145
[4]  
BARIN I, 1973, THERMOCHEMICAL PROPE, P616
[5]  
BEREZHNOI AA, 1981, OPT SPEKTROSK+, V50, P906
[6]  
BOKOV VA, 1961, FIZ TVERD TELA, V3, P841
[7]   GROWTH OF SINGLE CRYSTALS OF PB3MGNB2O9 BY KYROPOULOS TECHNIQUE [J].
BONNER, WA ;
VANUITER.LG .
MATERIALS RESEARCH BULLETIN, 1967, 2 (01) :131-&
[8]   DETERMINATION OF THE PHASE-DIAGRAMS, PBO-PB(FE1/2NB1/2)O3 AND PBO-PB(MN1/2NB1/2)O3 [J].
BRUNSKILL, IH ;
TISSOT, P ;
SCHMID, H .
THERMOCHIMICA ACTA, 1981, 49 (2-3) :351-355
[9]   HIGH-TEMPERATURE SOLUTION GROWTH OF PB(FE0.5NB0.5)O3 AND PB(MN0.5NB0.5)O3 CRYSTALS [J].
BRUNSKILL, IH ;
BOUTELLIER, R ;
DEPMEIER, W ;
SCHMID, H ;
SCHEEL, HJ .
JOURNAL OF CRYSTAL GROWTH, 1982, 56 (03) :541-546
[10]  
BURUS G, 1983, SOLID STATE COMMUN, V48, P853