CATALYTIC CERAMIC FILTERS FOR FLUE-GAS CLEANING .1. PREPARATION AND CHARACTERIZATION

This paper deals with the preparation and the characterization of ceramic porous filters, whose pores were deposited with a gamma-Al2O3 layer via the so-called ''urea method'', in order to increase their specific surface area. Once activated with a suitable catalytic principle, these filters can find a potential application in flue gas cleaning according to a combined action: mechanical particulate removal + catalytic abatement of chemical pollutants (nitrogen oxides, volatile organic compounds, etc.). Both the obtained filters and the bulk gamma-Al2O3 powder synthesized through the above method, were characterized from either a structural (BET surface area measurement, Hg porosimetry, differential thermal analysis-thermal gravimetry analysis, X-ray diffraction, scanning electron microscopy (SEM) observation, gas permeation) or a catalytic viewpoint. In this last context, isopropyl alcohol dehydration was chosen as a model reaction since it is directly catalyzed by gamma-Al2O3 (thanks to its acidic properties) with no need of further catalytic activation. A reaction mechanism is proposed for the test reaction, based on the existence of two types of active sites (A and B). On A-sites isopropyl alcohol gives an intermediate adsorbate and decomposes provided vicinal B-sites are available for water adsorption. A kinetic rate expression is worked out on the basis of experimental runs performed on a batch-operated differential reactor. The knowledge of this rate expression and of the structural characterization parameters are of major importance for the interpretation and the modeling of the results of a pilot-plant study on the above filters, performed using the same model reaction and presented in part 2 of this series. The urea method is demonstrated to be a reliable tool to deposit a gamma-Al2O3 layer all over the pore walls of the filter, markedly increasing its specific surface area. Drawbacks of the procedure employed are though the occurrence of pore blocking after a few deposition cycles and the occasional presence of cracks in the deposited layer.