O-18/SIMS CHARACTERIZATION OF THE GROWTH-MECHANISM OF DOPED AND UNDOPED ALPHA-AL2O3

被引：264

作者：

PINT, BA ^{[1
]}

MARTIN, JR ^{[1
]}

HOBBS, LW ^{[1
]}

机构：

[1] MIT,CTR MAT SCI & ENGN,SURFACE FACIL,CAMBRIDGE,MA 02139

来源：

OXIDATION OF METALS | 1993年 / 39卷 / 3-4期

关键词：

ALPHA-AL2O3; O-18/SIMS; REACTIVE ELEMENT EFFECT; FECRAL; BETA-NIAL;

D O I：

10.1007/BF00665610

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Sequential oxidation experiments at 1200-degrees-C and 1500-degrees-C using O-16 and >95% O-18-enriched environments were conducted on undoped and Y- and Zr-doped beta-NiAl and FeCrAl alloys. After oxidation, samples were analyzed by SIMS sputter depth profiling. At 1200-degrees-C, a clear pattern was established where the undoped alpha-Al2O3 was found to grow by the simultaneous transport of both Al and O. Zr-doped alpha-Al2O3 was found to grow mainly by the inward transport of oxygen. The profiles in all cases indicate O diffusion primarily by short-circuit pathways. Results at 1500-degrees-C (only on beta-NiAl) indicated a similar behavior but were less conclusive. Y and Zr were found to segregate to the oxide grain boundaries at 1200-degrees-C and 1500-degrees-C The segregation of these dopants is believed to impede the cation transport in the alpha-Al2O3 scale and thereby change the oxidation mechanism.

引用

页码：167 / 195

页数：29

共 44 条

[1] [Anonymous], UNPUB
[2] ATKINSON A, 1985, NATO ASI SER B-PHYS, V129, P285
[3] TRACER ISOTOPE DISTRIBUTION IN GROWING OXIDE SCALES
BASU, SN
HALLORAN, JW
[J]. OXIDATION OF METALS, 1987, 27 (3-4): : 143 - 155
[4] INFLUENCE OF SURFACE-AREA AND ADDITIVES ON THE THERMAL-STABILITY OF TRANSITION ALUMINA CATALYST SUPPORTS .1. KINETIC DATA
BURTIN, P
BRUNELLE, JP
PIJOLAT, M
SOUSTELLE, M
[J]. APPLIED CATALYSIS, 1987, 34 (1-2): : 225 - 238
[5] THE INFLUENCE OF IMPLANTED YTTRIUM ON THE MECHANISM OF GROWTH OF CR2O3 ON CR
COTELL, CM
YUREK, GJ
HUSSEY, RJ
MITCHELL, DF
GRAHAM, MJ
[J]. JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1987, 134 (07) : 1871 - 1872
[6] COTELL CM, 1990, OXID MET, V34, P173, DOI 10.1007/BF00665014
[7] INFLUENCE OF YTTRIUM ADDITIONS ON OXIDE-SCALE ADHESION TO AN IRON-CHROMIUM-ALUMINUM ALLOY
GOLIGHTLY, FA
STOTT, FH
WOOD, GC
[J]. OXIDATION OF METALS, 1976, 10 (03): : 163 - 187
[8] APPLICATION OF AUGER-ELECTRON SPECTROSCOPY AND INERT METAL MARKER TECHNIQUES TO DETERMINE METAL AND OXYGEN-TRANSPORT IN OXIDE-FILMS ON METALS
HINDAM, HM
SMELTZER, WW
[J]. OXIDATION OF METALS, 1980, 14 (04): : 337 - 349
[9] HOBBS LW, 1983, HIGH TEMPERATURE COR, P76
[10] FORMATION OF ALUMINUM-OXIDE SCALES IN SULFUR-CONTAINING HIGH-TEMPERATURE ENVIRONMENTS
HUANG, TT
RICHTER, R
CHANG, YL
PFENDER, E
[J]. METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1985, 16 (11): : 2051 - 2059

← 1 2 3 4 5 →