DURABILITY OF AN LA2ZR2O7 WASTE FORM IN WATER

被引：21

作者：

HAYAKAWA, I

KAMIZONO, H

机构：

[1] Department of Environmental Safety Research, Japan Atomic Energy Research Institute, Ibaraki-ken, 319-11, Tokai-mura

来源：

JOURNAL OF MATERIALS SCIENCE | 1993年 / 28卷 / 02期

关键词：

Lanthanum zirconate;

D O I：

10.1007/BF00357832

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The effects of time, temperature and pH on the leaching rates of an La2Zr2O7 waste form were studied. The leaching rates of each constituent measured in deionized water and an alkaline solution (pH = 10) were less than about 10(-5) g m-2 d-1 at 90-degrees-C and were smaller than those in an acid solution (pH = 1) by one order of magnitude. It was found that the leaching rate of zirconium obtained after immersion for 34 days decreases with increasing temperature in an acid solution. This exceptional phenomenon is attributed to the formation and decomposition of zirconium complexes with CO32- ligands.

引用

页码：513 / 517

页数：5

共 11 条

[1]

BAES CF, 1976, HYDROLYSIS CATIONS, P149

[2]

BRADLEY DC, 1973, COMPREHENSIVE INORGA, P454

[3]

Brookins D.G, 1988, EH PH DIAGRAMS GEOCH, P116, DOI [10.1007/978-3-642-73093-147.0, DOI 10.1007/978-3-642-73093-147.0]

[4]

HAYAKAWA I, 1991, 15TH INT C SCI BAS N

[5]

HAYAKAWA I, 1991, 3RD P INT S ADV NUCL, P408

[6] DURABILITY OF ZIRCONIUM-CONTAINING CERAMIC WASTE FORMS IN WATER [J].

KAMIZONO, H ;

HAYAKAWA, I ;

MURAOKA, S .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1991, 74 (04) :863-864

[7]

KAWAKUBO T, 1990, ZAIRYO, V39, P78

[8]

Kingery W.D., 1960, INTRO CERAMICS, P99

[9] FLUORITE TYPE PHASE IN NUCLEAR WASTE CERAMICS WITH HIGH ZIRCONIA AND ALUMINA CONTENTS [J].

MUROMURA, T ;

HINATSU, Y .

JOURNAL OF NUCLEAR MATERIALS, 1987, 151 (01) :55-62

[10] DISSOLUTION OF ALUMINUM-BASED, TITANIUM-BASED, AND ZIRCONIUM-BASED CRYSTALLINE WASTE FORM COMPONENTS UNDER HYDROTHERMAL CONDITIONS [J].

SCHEETZ, BE ;

WHITE, WB ;

ATKINSON, SD .

NUCLEAR TECHNOLOGY, 1982, 56 (02) :289-296

← 1 2 →