THE INTERACTION OF CU(100)-FE SURFACES WITH OXYGEN STUDIED BY X-RAY PHOTOELECTRON-SPECTROSCOPY

被引:38
作者
DENDAAS, H [1 ]
PASSACANTANDO, M [1 ]
LOZZI, L [1 ]
SANTUCCI, S [1 ]
PICOZZI, P [1 ]
机构
[1] UNIV UTRECHT, DEBYE INST, DIV SURFACE SCI, 3508 TB UTRECHT, NETHERLANDS
关键词
D O I
10.1016/0039-6028(94)90285-2
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
The oxidation of Cu(100)-Fe surfaces was studied using XPS. Surfaces containing 0-10 ML of iron were oxidised at room temperature exposing 2 Pa . s of oxygen. For all surfaces evidence for Fe2O3 was found. For surfaces containing more than 2 ML of iron, metallic Fe2p3/2 and 2p1/2 signatures were observed. The analysis of the change of the 2p peak shape of a surface containing 1 ML of Fe as a function of different oxygen coverages showed that oxidation proceeds via an intermediate containing both Fe2+ and Fe3+.
引用
收藏
页码:295 / 302
页数:8
相关论文
共 16 条
[1]   NONPSEUDOMORPHIC AND SURFACE-RECONSTRUCTED ULTRATHIN EPITAXIAL FCC FE FILMS ON CU(100) [J].
BAYER, P ;
MULLER, S ;
SCHMAILZL, P ;
HEINZ, K .
PHYSICAL REVIEW B, 1993, 48 (23) :17611-17614
[2]  
Chastain J., 1992, PERKIN ELMER CORP, V40, P221, DOI DOI 10.1016/0009-2614(83)80259-0
[3]   OXIDATION OF ULTRATHIN IRON LAYERS ON CU(100) - COMPOSITION OF THE OXIDE-FILMS [J].
DENDAAS, H ;
GIJZEMAN, OLJ ;
GEUS, JW .
SURFACE SCIENCE, 1993, 285 (1-2) :15-26
[4]   LOW-ENERGY AUGER-ELECTRON SPECTROSCOPY OF IRON-OXIDE - OXIDATION OF ONE MONOLAYER OF IRON ON CU(100) [J].
DENDAAS, H ;
GIJZEMAN, OLJ ;
GEUS, JW .
SURFACE SCIENCE, 1993, 290 (1-2) :26-34
[5]  
KISHI K, 1990, SURF SCI, V227, P97, DOI 10.1016/0039-6028(90)90396-P
[6]   GEOMETRIC STRUCTURE OF THE ALPHA-FE2O3(001) SURFACE - A LEED AND XPS STUDY [J].
KURTZ, RL ;
HENRICH, VE .
SURFACE SCIENCE, 1983, 129 (2-3) :345-354
[7]   ANOMALOUS L3-L2 WHITE-LINE RATIOS IN THE 3D TRANSITION-METALS [J].
LEAPMAN, RD ;
GRUNES, LA .
PHYSICAL REVIEW LETTERS, 1980, 45 (05) :397-401
[8]  
LEIBBRANDT GWR, 1991, SURF SCI, V244, pL101, DOI 10.1016/0039-6028(91)90161-K
[9]   INTERACTION OF O2 WITH THE FE0.84CR0.16(001) SURFACE STUDIED BY PHOTOELECTRON-SPECTROSCOPY [J].
LINCE, JR ;
DIDZIULIS, SV ;
SHUH, DK ;
DURBIN, TD ;
YARMOFF, JA .
SURFACE SCIENCE, 1992, 277 (1-2) :43-63
[10]   XPS STUDY OF IN-SITU OXIDATION OF AN FE-CR ALLOY BY LOW-PRESSURE OXYGEN IN THE PRESENCE OF WATER-VAPOR [J].
PALACIO, C ;
MATHIEU, HJ ;
STAMBOULI, V ;
LANDOLT, D .
SURFACE SCIENCE, 1993, 295 (1-2) :251-262