TITANIUM ALUMINIDES BY HOT ISOSTATIC PRESSING OF COLD-EXTRUDED TITANIUM ALUMINUM POWDER MIXTURES

被引：14

作者：

DAHMS, M

SEEGER, J

SMARSLY, W

WILDHAGEN, B

机构：

[1] TECH UNIV HAMBURG, W-2100 HAMBURG 90, GERMANY

[2] MOTOREN & TURBINEN UNION MUNCHEN GMBH, W-8000 MUNICH 50, GERMANY

来源：

ISIJ INTERNATIONAL | 1991年 / 31卷 / 10期

关键词：

TIAL; POWDER METALLURGY; EXTRUSION; REACTIVE HIP; MICROCRACKING; DYNAMIC RECRYSTALLIZATION;

D O I：

10.2355/isijinternational.31.1093

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Gamma-base titanium-aluminides were produced by reactive hot isostatic pressing (RHIP) of cold extruded titanium-aluminium elemental powder mixtures. Various RHIP temperatures as well as additional heat treatments were applied in order to obtain different microstructures. Compression samples were tested between room temperature and 900-degrees-C. Changes in microstructure during compression such as microcracking, inhomogeneous deformation and dynamic recrystallization were investigated. The measured properties are discussed with respect to microstructure.

引用

页码：1093 / 1099

页数：7

共 24 条

[1] ELEMENTAL POWDER APPROACHES TO NI3AL-MATRIX COMPOSITES [J].

BOSE, A ;

MOORE, B ;

GERMAN, RM ;

STOLOFF, NS .

JOURNAL OF METALS, 1988, 40 (09) :14-17

[2]

COLVIN G, 1990, IN PRESS S MICROSTRU

[3]

DAHMS M, 1990, SOLID STATE POWDER PROCESSING, P77

[4] FORMATION OF TITANIUM ALUMINIDES BY HEAT-TREATMENT OF EXTRUDED ELEMENTAL POWDERS [J].

DAHMS, M .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1989, 110 :L5-L8

[5]

DAHMS M, 1990, ADV MATER PROCESS, V1, P297

[6] FRACTURE-BEHAVIOR OF A TI-48.5AL-1MN ALLOY [J].

DOGAN, B ;

WAGNER, R ;

BEAVEN, PA .

SCRIPTA METALLURGICA ET MATERIALIA, 1991, 25 (04) :773-778

[7]

FREEMAN W, 1989, GORHAM ALUMINIDES C

[8]

FUKOTOMI H, 1990, Z METALLKD, V81, P272

[9]

GERMAN RM, 1990, P WORLD C POWDER MET, V1, P310

[10]

HARTIG C, 1989, 6TH P WORLD C TIT CA, V2, P1021

← 1 2 3 →