THE FRACTURE OF ORDERED (FE,CO)3V

被引:14
作者
LIU, CT [1 ]
SCHULSON, EM [1 ]
机构
[1] DARTMOUTH COLL, THAYER SCH ENGN, HANOVER, NH 03755 USA
来源
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 1984年 / 15卷 / 04期
关键词
VANADIUM METALLOGRAPHY - Microstructures;
D O I
10.1007/BF02644201
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Observations have been made of fracture surfaces deformed at low strain rates (3. 3 and 42 multiplied by 10** minus **3s** minus **1) in tension at temperatures from 20 to 1000 degree C, that is, above and below the order/disorder transformation temperature of 950 plus or minus 10 degree C. From 20 to 700 degree C, transgranular fracture occurs via the nucleation, growth, and coalescence of microvoids; high ductilities are obtained (34 to 44 pct). From 700 to 960 degree C, the fracture mode changes from transgranular to intergranular and ductility falls to a minimum of 4 pct. At 1000 degree C a third mode operates consisting of localized dynamic recrystallization followed by boundary sliding of recrystallized grains; ductility rises sharply. The underlying mechanisms are supported through additional experiments performed at higher strain rates.
引用
收藏
页码:701 / 706
页数:6
相关论文
共 14 条
[1]   HIGH CYCLE FATIGUE OF (FE, NI, CO)3V TYPE ALLOYS [J].
ASHOK, S ;
KAIN, K ;
TARTAGLIA, JM ;
STOLOFF, NS .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1983, 14 (10) :1997-2003
[2]  
BRASKI DN, 1982, J NUCL MATER, V103, P1199
[3]   THE MICROSTRUCTURE OF ORDERED (CO0.78FE0.22)3V ALLOY [J].
BRASKI, DN ;
CARPENTER, RW ;
BENTLEY, J .
ACTA METALLURGICA, 1982, 30 (04) :799-812
[4]   EFFECT OF THORIUM ADDITIONS ON METALLURGICAL AND MECHANICAL-PROPERTIES OF IR-0.3 PCT-W ALLOYS [J].
LIU, CT ;
INOUYE, H ;
SCHAFFHAUSER, AC .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1981, 12 (06) :993-1002
[5]   DEVELOPMENT OF DUCTILE LONG-RANGE ORDERED ALLOYS FOR FUSION-REACTOR SYSTEMS [J].
LIU, CT .
JOURNAL OF NUCLEAR MATERIALS, 1979, 85-6 (DEC) :907-911
[6]   CONTROL OF ORDERED STRUCTURE AND DUCTILITY OF (FE,CO,NI)3V ALLOYS [J].
LIU, CT ;
INOUYE, H .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1979, 10 (10) :1515-1525
[7]  
LIU CT, 1981, J NUCL MATER, V103, P1205
[8]  
LIU CT, 1968, T ASM, V61, P156
[9]  
LIU CT, 1980, UNPUB
[10]  
LIU CT, INT MET REV