DEVELOPMENT OF 10KA CLASS NB3AL SUPERCONDUCTING CABLE BY JELLY-ROLL PROCESS

被引：11

作者：

ANDO, T ^{[1
]}

TAKAHASHI, Y ^{[1
]}

NISHI, M ^{[1
]}

YAMADA, Y ^{[1
]}

OHMATSU, K ^{[1
]}

NAGATA, M ^{[1
]}

机构：

[1] SUMITOMO ELECT IND LTD,OSAKA RES LABS,KONOHANA KU,OSAKA 554,JAPAN

来源：

IEEE TRANSACTIONS ON MAGNETICS | 1991年 / 27卷 / 02期

关键词：

D O I：

10.1109/20.133535

中图分类号：

TM [电工技术]; TN [电子技术、通信技术];

学科分类号：

0808 ; 0809 ;

摘要：

A multifilamentary Cu/Nb3Al composite strand was developed, with a non-copper critical current density of more than 400 A/mm2 at 12T, by Jelly-roll process. A 10 kA cable-in-conduit conductor was fabricated to demonstrate the applicability to fusion magnets. The cable had 324 strands, and a circular CuNi seamless pipe was used as the conduit. The strand diameter was 0.88 mm and the filament diameter was 28-mu-m. The heat treatment was performed at 820-degrees-C for 2 hr.

引用

页码：1775 / 1778

页数：4

共 7 条

[1] EFFECT OF THE THICKNESS OF ALUMINUM LAYER ON THE TRANSPORT-PROPERTIES OF NB3AL SUPERCONDUCTING WIRES [J].

ANNARATONE, B ;

BRUZZESE, R ;

CERESARA, S ;

PERICOLIRIDOLFINI, V ;

PITTO, G ;

SACCHETTI, N .

IEEE TRANSACTIONS ON MAGNETICS, 1981, 17 (01) :1000-1001

[2]

Ekin J. W., 1984, ADV CRYOGEN ENG, V30, P823

[3] FABRICATION OF NB3AL AND NB3(AL,GE) SUPERCONDUCTING COMPOSITE TAPES BY ELECTRON-BEAM IRRADIATION [J].

KUMAKURA, H ;

TOGANO, K ;

TACHIKAWA, K ;

TSUKAMOTO, S ;

IRIE, H .

APPLIED PHYSICS LETTERS, 1986, 49 (01) :46-48

[4]

OHMATSU K, 1989, SEP M SUP MAT MAGN T

[5]

SAITO S, 1989, 11TH INT C MAGN TECH

[6] IMPROVED HIGH-FIELD PERFORMANCE OF NB-AL POWDER-METALLURGY PROCESSED SUPERCONDUCTING WIRES [J].

THIEME, CLH ;

POURRAHIMI, S ;

SCHWARTZ, BB ;

FONER, S .

APPLIED PHYSICS LETTERS, 1984, 44 (02) :260-262

[7] TRANSVERSE STRESS EFFECT ON THE CRITICAL CURRENT OF JELLY-ROLL MULTIFILAMENTARY NB3AL WIRES [J].

ZERITIS, D ;

ANDO, T ;

TAKAHASHI, Y ;

NISHI, M ;

NAKAJIMA, H ;

SHIMAMOTO, S .

APPLIED PHYSICS LETTERS, 1990, 57 (05) :506-507

← 1 →