POLYURETHANE IONOMERS FROM CYCLOALIPHATIC DIISOCYANATE AND POLYTETRAMETHYLENE GLYCOL

Segmented polyurethane (PU) ionomers were prepared from cycloaliphatic diisocyanate [methylene bis(4-cyclohexyl isocyanate) (H12MDI) and isophoron diisocyanate (IPDI)] and polytetramethylene glycol (PTMG) by using an anionic-type chain extender, viz., dimethylol propionic acid (DMPA). The effect of ionic content and butanediol (BD) on the state of dispersion and physical properties of emulsion-cast film was determined using Autosizer, transmission electron microscopy (TEM), Instron, and Rheovibron. With increased incorporations of DMPA in PU, particle size of emulsion decreased asymptotically, tensile modulus and strength increased, and the glass transition temperature (Tg) moved toward the higher temperature. On the other hand, with increased incorporation of BD in PU, particle size of emulsion, tensile modulus, and strength of the emulsion cast film increased, and the major transition of soft segment moved toward higher temperature. With regard to the structural effect of the isocyanate, H12MDI gave finer dispersion and better mechanical properties over IPDI.