NACL-INDUCED HOT CORROSION OF A TITANIUM ALUMINIDE ALLOY

被引：65

作者：

YAO, Z

MAREK, M

机构：

[1] School of Materials Science and Engineering, Georgia Institute of Technology, Atlanta

来源：

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 1995年 / 192卷

关键词：

SODIUM; CHLORINE; CORROSION; TITANIUM; ALUMINUM; ALLOYS;

D O I：

10.1016/0921-5093(95)03345-9

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

NaCl-induced hot corrosion of a TiAl-based intermetallic, Ti-47at.%Al-2at.%Nb-2at.%Mn + 7 vol.% TiB2, was studied. Sodium chloride was vapor deposited on the surface of the specimens. The reaction of the metal, oxygen and deposited sodium chloride caused the formation of a non-protective scale and accelerated the oxidation of the alloy. Pits and possible grain boundary attack were observed on the corroded surfaces. Oxygen-free exposure showed no corrosion of the TiAl alloy due to NaCl at temperatures below and above the melting temperature of NaCl. Thermodynamic calculations were carried out to predict the possible corrosion products. The corrosion mechanisms are discussed.

引用

页码：994 / 1000

页数：7

共 11 条

[1] CORROSION BEHAVIOR OF AUSTENITIC STAINLESS-STEELS IN THE HIGH CHLORIDE-CONTAINING ENVIRONMENT [J].

FUJIKAWA, H ;

MARUYAMA, N .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1989, 120 :301-306

[2]

HANCOCK P, 1987, MATER SCI TECHNOL, V3, P540

[3] EFFECTS OF ALLOYING ELEMENTS ON NACL-INDUCED HOT CORROSION OF STAINLESS-STEELS [J].

HIRAMATSU, N ;

UEMATSU, Y ;

TANAKA, T ;

KINUGASA, M .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1989, 120 (1 -2 pt 1) :319-328

[4]

LAI GY, 1991, AM SOC MECH ENG PAP, P1

[5] A REVIEW OF ADVANCES IN HIGH-TEMPERATURE CORROSION [J].

MEIER, GH .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1989, 120 :1-11

[6] CHEMISTRY AND ELECTROCHEMISTRY OF THE HOT CORROSION OF METALS [J].

RAPP, RA .

CORROSION, 1986, 42 (10) :568-577

[7]

SINATA Y, 1990, OXID MET, V26, P313

[8]

STRINGER J, 1987, MAT SCI TECHNOL, V3, P483

[9] OXIDATION BEHAVIOR OF TIAL AT HIGH-TEMPERATURES IN PURIFIED OXYGEN [J].

TANIGUCHI, S ;

SHIBATA, T ;

ITOH, S .

MATERIALS TRANSACTIONS JIM, 1991, 32 (02) :151-156

[10]

TORTORELLI PF, 1991, ENV EFFECTS ADV MAT, P91

← 1 2 →