NONISOTHERMAL DEGRADATION KINETICS OF GLASS-REINFORCED EPOXY-RESIN

被引：11

作者：

BUDRUGEAC, P

机构：

[1] ICPE-Research Institute for Electrical Engineering, Bucharest CP, 79623, Bd. T. Vladimirescu nr. 45-47

来源：

THERMOCHIMICA ACTA | 1993年 / 221卷 / 02期

关键词：

D O I：

10.1016/0040-6031(93)85068-K

中图分类号：

O414.1 [热力学];

学科分类号：

摘要：

The results obtained from the thermal analysis (TG, DTG, DTA) of glass-reinforced epoxy resin are presented. It has been shown that on heating in air up to 320-degrees-C, an exothermic process with formation of volatile products takes place. The non-isothermal kinetic parameters of this process have been determined by various methods.

引用

收藏

页码：229 / 236

页数：8

相关论文

共 19 条

[1] THERMAL-DEGRADATION OF POLYCHLOROPRENE RUBBER [J].

BUDRUGEAC, P ;

CIUTACU, S .

POLYMER DEGRADATION AND STABILITY, 1991, 33 (03) :377-386

[2]

BUDRUGEAC P, IN PRESS THERMOCHIM

[3] BASIC PROGRAM TO DISCRIMINATE AMONG MECHANISMS OF SOLID GAS DECOMPOSITION (DISCRIM-2) [J].

CARP, O ;

SEGAL, E .

THERMOCHIMICA ACTA, 1991, 185 (01) :111-127

[4] ACCELERATED THERMAL AGING OF ETHYLENE-PROPYLENE RUBBER IN PRESSURIZED OXYGEN [J].

CIUTACU, S ;

BUDRUGEAC, P ;

MARES, G ;

BOCONCIOS, I .

POLYMER DEGRADATION AND STABILITY, 1990, 29 (03) :321-329

[5] ACCELERATED THERMAL AGING OF GLASS-REINFORCED EPOXY-RESIN UNDER OXYGEN-PRESSURE [J].

CIUTACU, S ;

BUDRUGEAC, P ;

NICULAE, I .

POLYMER DEGRADATION AND STABILITY, 1991, 31 (03) :365-372

[6] KINETIC PARAMETERS FROM THERMOGRAVIMETRIC DATA [J].

COATS, AW ;

REDFERN, JP .

NATURE, 1964, 201 (491) :68-&

[7] BASIC VERSATILE PROGRAM FOR NONISOTHERMAL KINETICS .2. [J].

DRAGOE, N ;

SEGAL, E .

THERMOCHIMICA ACTA, 1991, 185 (01) :129-134

[8] DEGRADATION KINETICS APPLIED TO LIFETIME PREDICTIONS OF POLYMERS [J].

FLYNN, JH .

POLYMER ENGINEERING AND SCIENCE, 1980, 20 (10) :675-677

[9] GENERAL TREATMENT OF THERMOGRAVIMETRY OF POLYMERS [J].

FLYNN, JH ;

WALL, LA .

JOURNAL OF RESEARCH OF THE NATIONAL BUREAU OF STANDARDS SECTION A-PHYSICS AND CHEMISTRY, 1966, A 70 (06) :487-+

[10]

FLYNNJH, 1977, THERMAL METHODS POLY, P163