Y2BACUO5 PARTICLE COARSENING DURING MELT PROCESSING OF YBA2CU3O7-X

被引：11

作者：

VARANASI, C

MCGINN, PJ

机构：

[1] Center for Materials Science and Engineering, Department of Electrical Engineering, University of Notre Dame, Notre Dame, 46556, IN

来源：

JOURNAL OF ELECTRONIC MATERIALS | 1993年 / 22卷 / 10期

关键词：

123; SUPERCONDUCTORS; COARSENING; MELT PROCESSING; 2ND PHASE ADDITIONS; SOLIDIFICATION;

D O I：

10.1007/BF02818068

中图分类号：

TM [电工技术]; TN [电子技术、通信技术];

学科分类号：

0808 ; 0809 ;

摘要：

Quenching experiments were carried out to study the coarsening phenomena of Y2BaCuO5 (211) particles in liquid (Ba3Cu5O8) which form as a result of the peritectic decomposition of YBa2Cu3O7-x (123) above 1010-degrees-C. The morphology of 211 particles was observed to become more acicular as the time of hold increased at 1040-degrees-C, showing an anisotropic growth rate of the 211 particles in the liquid. Also, the coarsening rate was found to be increased in the presence of excess added liquid phase (BaCu5O8) in the 123. Externally added 211 particles were found to act as heterogeneous nucleation sites for the peritectically formed 211. The observed cored 211 morphology development in the Er 211 doped, melt textured, Y 123 pellets was explained on the basis of ripening of 211 particles. Reduced coarsening of 211 particles was observed in the presence of 0.5 wt.% Pt doping.

引用

页码：1251 / 1257

页数：7

共 26 条

[1] EFFECT OF VOLUME FRACTION ON PARTICLE COARSENING - THEORETICAL CONSIDERATIONS [J].

ARDELL, AJ .

ACTA METALLURGICA, 1972, 20 (01) :61-&

[2]

BALKIN D, UNPUB

[3] MECHANISM FOR THE PERITECTIC REACTION AND GROWTH OF ALIGNED GRAINS IN YBA2CU3O6+X [J].

BATEMAN, CA ;

ZHANG, LJ ;

CHAN, HM ;

HARMER, MP .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1992, 75 (05) :1281-1283

[4] SEMISOLID SOLIDIFICATION OF HIGH-TEMPERATURE SUPERCONDUCTING OXIDES [J].

CIMA, MJ ;

FLEMINGS, MC ;

FIGUEREDO, AM ;

NAKADE, M ;

ISHII, H ;

BRODY, HD ;

HAGGERTY, JS .

JOURNAL OF APPLIED PHYSICS, 1992, 72 (01) :179-190

[5] MASS-TRANSFER IN A ERBA2CU3O7 PELLET PARTIALLY MELTED IN A THERMAL-GRADIENT [J].

DUBE, D ;

ARSENAULT, B ;

GELINAS, C ;

LAMBERT, P .

MATERIALS LETTERS, 1992, 15 (1-2) :1-7

[6] EFFECT OF Y2BACUO5 ON FRACTURE-TOUGHNESS OF YBCO PREPARED BY A MPMG PROCESS [J].

FUJIMOTO, H ;

MURAKAMI, M ;

KOSHIZUKA, N .

PHYSICA C, 1992, 203 (1-2) :103-110

[7]

GURLAND J, 1954, JOM-J MIN MET MAT S, V6, P285

[8] REACTION-MECHANISM OF Y-SYSTEM SUPERCONDUCTORS IN THE MPMG METHOD [J].

IZUMI, T ;

NAKAMURA, Y ;

SUNG, TH ;

SHIOHARA, Y .

JOURNAL OF MATERIALS RESEARCH, 1992, 7 (04) :801-807

[9]

IZUMI T, 1992, P INT WORKS SUP PITT, P280

[10] HIGH CRITICAL CURRENTS IN Y-BA-CU-O SUPERCONDUCTORS [J].

JIN, S ;

TIEFEL, TH ;

SHERWOOD, RC ;

DAVIS, ME ;

VANDOVER, RB ;

KAMMLOTT, GW ;

FASTNACHT, RA ;

KEITH, HD .

APPLIED PHYSICS LETTERS, 1988, 52 (24) :2074-2076

← 1 2 3 →