GLASS STRENGTHENING BY POLYMER-DERIVED CERAMIC COATINGS

被引：22

作者：

BLUM, YD

PLATZ, RM

CRAWFORD, EJ

机构：

[1] Sri International, Menlo Park, California

来源：

JOURNAL OF THE AMERICAN CERAMIC SOCIETY | 1990年 / 73卷 / 01期

关键词：

coatings; glass; polymers; silazanes; strength;

D O I：

10.1111/j.1151-2916.1990.tb05116.x

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Polysilazane‐derived ceramic coatings in the form of thin films (0.1 to 4 μm) — fabricated by dipcoating soda‐lime rods with preceramic polymer solutions, followed by pyrolysis — increased the strength of the glass rods. Strengths up to 414 ± 57 MPa were obtained, 2.3 and 3.3 times higher than the strengths of uncoated/annealed and as‐received rods, respectively. As‐received coated glass was stronger than coated annealed glass. Microstructural damage was not observed in the optimal coatings. Copyright © 1990, Wiley Blackwell. All rights reserved

引用

页码：170 / 172

页数：3

共 11 条

[1]

BLUM YD, 1986, BETTER CERAMICS CHEM, V73, P389

[2]

BLUM YD, 1987, PCT WO8705298 INT PA

[3]

BLUM YD, 1988, UNPUB POLYM PRECURSO

[4]

CRAWFORD JE, 1974, Patent No. 3811921

[5] STRENGTHENING OF SILICA GLASS BY GEL-DERIVED COATINGS [J].

FABES, BD ;

DOYLE, WF ;

ZELINSKI, BJJ ;

SILVERMAN, LA ;

UHLMANN, DR .

JOURNAL OF NON-CRYSTALLINE SOLIDS, 1986, 82 (1-3) :349-355

[6] THE CORROSION-RESISTANCE OF AN ALUMINUM-ALLOY COATED WITH POLYSILAZANE-DERIVED CERAMICS [J].

LENHART, SJ ;

BLUM, YD ;

LAINE, RM .

CORROSION, 1989, 45 (06) :503-506

[7] SLOW FRACTURE MODEL BASED ON STRAINED SILICATE STRUCTURES [J].

MICHALSKE, TA ;

BUNKER, BC .

JOURNAL OF APPLIED PHYSICS, 1984, 56 (10) :2686-2693

[8]

Shand E.B., 1985, GLASS ENG HDB

[9]

SHINKAI N, 1975, REP RES LAB ASAHI GL, V25, P1

[10]

SOZANSKI MR, 1987, AM CERAM SOC BULL, V66, P1630

← 1 2 →