FAILURE PREDICTION IN TOUGHENED EPOXY-RESINS

A major toughening mechanism causing increased toughness is the shear deformation process occurring near the crack tip. The effect of such a deformation process is to blunt the crack tip and increase the size of the plastic zone. Several models are available to predict the toughness on the basis of plastic zone size, crack tip opening displacement or crack tip radius, but these are only applicable to Mode I crack extension. Also, most of these approaches use only one stress component which is normal to the crack plane to predict the fracture toughness. The present paper reviews the existing models and suggests a criterion based on the phenomenological approach to failure in order to study the yielding and fracture toughness behavior of both unmodified and modified epoxies. The proposed yield and fracture criteria give predictions in good agreement with experimental results.