EFFECT OF MORPHOLOGY OF POLYANILINE ON ITS DISCHARGE CHARACTERISTICS IN NONAQUEOUS ELECTROLYTE

被引:22
作者
KANAMURA, K
KAWAI, Y
YONEZAWA, S
TAKEHARA, Z
机构
[1] Division of Energy and Hydrocarbon Chemistry, Graduate School of Engineering, Kyoto University Yoshida-honmachi
关键词
D O I
10.1149/1.2048661
中图分类号
O646 [电化学、电解、磁化学];
学科分类号
081704 ;
摘要
The discharge and charge performance of polyaniline which has a fibrous morphology was investigated from microscopic current density and anion diffusion time constant measurements. The microscopic discharge current density is calculated from the radius of the polyaniline fibril, assuming the true electrode surface area corresponds to the surface area of the long polyaniline fibril (2 alpha L, L:the sum of the length of the polyaniline fibril). The time constant for the diffusion of anions in the polyaniline fibril was calculated from alpha(2)/D, where D is the diffusion coefficient and a is the polyaniline fibril radius. The diffusion coefficient was measured using an impedance method, and the alpha(2)/D parameter was calculated. Galvanostatic discharge and charge cycle tests were carried out to decide the performance of polyaniline cathodes with different fibril radii. From these experiments, it can be seen that the dependence of the discharge characteristics on the fibril radius is diminished by the positive dependencies of the diffusion coefficient and roughness of the polyaniline fibril on the fibril radius.
引用
收藏
页码:2894 / 2899
页数:6
相关论文
共 35 条
[1]   ELECTROCHEMICAL FABRICATION OF A POLYPYRROLE POLYTHIOPHENE P-N-JUNCTION DIODE [J].
AIZAWA, M ;
SHINOHARA, H ;
YAMADA, T ;
AKAGI, K ;
SHIRAKAWA, H .
SYNTHETIC METALS, 1987, 18 (1-3) :711-714
[2]   ALTERATION OF THE ION-EXCHANGE MECHANISM OF AN ELECTROACTIVE POLYMER BY MANIPULATION OF THE ACTIVE-SITE - PROBE BEAM DEFLECTION AND QUARTZ CRYSTAL MICROBALANCE STUDY OF POLY(ANILINE) AND POLY(N-METHYLANILINE) [J].
BARBERO, C ;
MIRAS, MC ;
HAAS, O ;
KOTZ, R .
JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 1991, 310 (1-2) :437-443
[3]   LIGHT-INDUCED ELECTRON-SPIN-RESONANCE IN POLYANILINE [J].
CROMACK, K ;
EPSTEIN, AJ ;
MASTERS, J ;
SUN, Y ;
MACDIARMID, AG .
SYNTHETIC METALS, 1991, 41 (1-2) :641-644
[4]   MORPHOLOGY OF ELECTROCHEMICALLY PREPARED POLYANILINE - INFLUENCE OF POLYMERIZATION PARAMETERS [J].
DESILVESTRO, J ;
SCHEIFELE, W .
JOURNAL OF MATERIALS CHEMISTRY, 1993, 3 (03) :263-272
[5]  
Evans G.P, 1990, ADV ELECTROCHEMICAL
[6]   AN IMPEDANCE STUDY OF POLYANILINE FILMS IN AQUEOUS AND ORGANIC SOLUTIONS [J].
FIORDIPONTI, P ;
PISTOIA, G .
ELECTROCHIMICA ACTA, 1989, 34 (02) :215-221
[7]  
FISCHER JE, 1991, MACROMOLECULES, V43, P661
[8]  
FOSONG W, 1988, MOL CRYST LIQ CRYST, V160, P175
[9]   SIMULATION AND OPTIMIZATION OF THE DUAL LITHIUM ION INSERTION CELL [J].
FULLER, TF ;
DOYLE, M ;
NEWMAN, J .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1994, 141 (01) :1-10
[10]   POLYANILINE - A HISTORICAL SURVEY [J].
GENIES, EM ;
BOYLE, A ;
LAPKOWSKI, M ;
TSINTAVIS, C .
SYNTHETIC METALS, 1990, 36 (02) :139-182