DYNAMIC FRACTURE-ANALYSIS BY MOIRE INTERFEROMETRY

被引：15

作者：

ARAKAWA, K ^{[1
]}

DRINNON, RH ^{[1
]}

KOSAI, M ^{[1
]}

KOBAYASHI, AS ^{[1
]}

机构：

[1] BOEING COMMERCIAL AIRPLANE CO,DEPT MECH ENGN,FU-10,SEATTLE,WA 98124

来源：

EXPERIMENTAL MECHANICS | 1991年 / 31卷 / 04期

关键词：

D O I：

10.1007/BF02325986

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Dynamic moire interferometry was used to measure separately the u- and v-displacement fields surrounding a rapidly propagating crack tip in Homalite-100 and 7075-T6 aluminum-alloy plates. These transient crack-tip-displacement data were then used to compute the dynamic stress-intensity factor and the remote stress component. J-integral values were also estimated using the static approximate procedure of Kang et al. This static analysis provided the correct J when the contour integral was taken within 3 mm of the crack tip.

引用

页码：306 / 309

页数：4

共 21 条

[1] DETERMINING K AND RELATED STRESS-FIELD PARAMETERS FROM DISPLACEMENT-FIELDS [J].

BARKER, DB ;

SANFORD, RJ ;

CHONA, R .

EXPERIMENTAL MECHANICS, 1985, 25 (04) :399-407

[2]

Bradley W.B., 1971, ENG FRAC MECH, V3, P317

[3] HRR FIELD OF A MOVING CRACK - AN EXPERIMENTAL-ANALYSIS [J].

DADKHAH, MS ;

KOBAYASHI, AS .

ENGINEERING FRACTURE MECHANICS, 1989, 34 (01) :253-262

[4]

DADKHAH MS, 1990, 9TH P INT C EXP MECH, V5, P1767

[5] DYNAMIC PHOTO-ELASTIC STUDIES OF FRACTURE [J].

DALLY, JW .

EXPERIMENTAL MECHANICS, 1979, 19 (10) :349-361

[6]

DEASON VA, 1991, OPT LASER ENG, V12, P173

[7]

DU J, 1990, MICROMECHANICS OF FAILURE OF QUASI-BRITTLE MATERIALS, P146

[8] SINGULAR BEHAVIOUR AT END OF A TENSILE CRACK IN A HARDENING MATERIAL [J].

HUTCHINSON, JW .

JOURNAL OF THE MECHANICS AND PHYSICS OF SOLIDS, 1968, 16 (01) :13-+

[9]

KALTHOFF JF, 1977, ASTM STP, V627, P161

[10] STABLE CRACK-GROWTH IN ALUMINUM TENSILE SPECIMENS [J].

KANG, BSJ ;

KOBAYASHI, AS ;

POST, D .

EXPERIMENTAL MECHANICS, 1987, 27 (03) :234-245

← 1 2 3 →