CORRELATION BETWEEN DUCTILITY AND ORDERING ENERGY OF NI3AL

被引：28

作者：

CHIBA, A

HANADA, S

WATANABE, S

机构：

[1] Institute for Materials Reseach, Tohoku University

来源：

MATERIALS TRANSACTIONS JIM | 1990年 / 31卷 / 09期

关键词：

ductilization mechanism; intermetallic compound; Ll[!sub]2[!/sub] ordered alloy; mechanical property; Ni[!sub]3[!/sub]Al; ordering energy;

D O I：

10.2320/matertrans1989.31.824

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Ductility improvement is investigated at room temperature in polycrystalline Ni3Al macroalloyed with Pd which has been revealed to have a strong tendency to substitute for the Ni site independent of the composition of the host elements. Pd-doped Ni3Al was successfully rolled by 10∽40% reduction in as-cast condition. It was found that the recrystallized Ni75Al23Pd2 exhibited elongation to fracture of 11%, whereas recrystallized Ni73Al25Pd2 did brittle fracture. It can be concluded that the ductility improvement of Ni3Al by macroalloying with Pd is attributable to degradation of the ordering energy, combined with decrease in Al content. © 1990, The Japan Institute of Metals. All rights reserved.

引用

页码：824 / 827

页数：4

共 17 条

[1]

ACKLAND GJ, 1989, HIGH TEMPERATURE ODE, V133, P105

[2] THE ORDER-DISORDER TRANSFORMATION IN NI3AL AND NI3AL-FE ALLOYS .2. PHASE-TRANSFORMATIONS AND MICROSTRUCTURES [J].

CAHN, RW ;

SIEMERS, PA ;

HALL, EL .

ACTA METALLURGICA, 1987, 35 (11) :2753-2764

[3] THE ORDER-DISORDER TRANSFORMATION IN NI3AL AND NI3AL-FE ALLOYS .1. DETERMINATION OF THE TRANSITION-TEMPERATURES AND THEIR RELATION TO DUCTILITY [J].

CAHN, RW ;

SIEMERS, PA ;

GEIGER, JE ;

BARDHAN, P .

ACTA METALLURGICA, 1987, 35 (11) :2737-2751

[4]

CHIBA A, IN PRESS ACTA METALL

[5] ANALYSIS OF GAMMA'/GAMMA-EQUILIBRIUM IN NI-AL-X ALLOYS BY THE CLUSTER VARIATION METHOD WITH THE LENNARD-JONES POTENTIAL [J].

ENOMOTO, M ;

HARADA, H .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1989, 20 (04) :649-664

[6]

FLINN PA, 1960, T AM I MIN MET ENG, V218, P145

[7]

GUARD RW, 1959, T AM I MIN MET ENG, V215, P807

[8]

HANADA S, 1986, J MATER SCI, V21, P302

[9]

JIA CC, 1990, THESIS TOHOKU U

[10] ON THE AVAILABILITY OF DISLOCATION REACTIONS AT GRAIN-BOUNDARIES IN CUBIC ORDERED ALLOYS [J].

KING, AH ;

YOO, MH .

SCRIPTA METALLURGICA, 1987, 21 (08) :1115-1119

← 1 2 →