MULLITE ALUMINA PARTICULATE COMPOSITES BY INFILTRATION PROCESSING .3. MECHANICAL-PROPERTIES

The effect of incorporating mullite into alumina by an infiltration process on the mechanical properties was investigated. Data for Young's modulus, strength, and fracture toughness for various composite compositions were compared with those for the unreinforced matrix (alumina). Measurements of Young's modulus by a resonance technique showed that the addition of mullite decreased Young's modulus. Up to 14 vol%, these changes were close to those expected, but above this mullite content, the decrease was more dramatic and indicated specimen damage during processing. The addition of mullite led, in some cases, to increases of more than 60% in both the strength (biaxial flexure) and indentation fracture toughness. These increases have been attributed to the method of introducing mullite and the resulting residual compressive surface stresses. The strength of the indented composite bodies deviated from the ideal behavior, indicating the probability of R-curve behavior in these materials.