THE MOSSBAUER SPECTRUM OF ILLITE

Eight illites were studied by Mossbauer spectroscopy at room temperature and 4.2 K. On the basis of their Fe contents, these illites can be divided into an Fe-rich (>5 wt% Fe) and an Fe-poor (<1 to approximately 3 wt% Fe) group. Mossbauer spectroscopy showed that the Fe-rich illites had lower proportions of divalent Fe than their Fe-poor counterparts. Slow paramagnetic relaxation was observed in the Fe-poor illites and must be accounted for when fitting the spectra. Two samples contained iron oxides that were superparamagnetic and thus, although contributing to the Fe3+ doublets, escaped detection at room temperature. Structural Fe3+ had a temperature-independent quadrupole splitting that was lower for the Fe-rich illites (0.59 mm/s) than that of the Fe-poor illites (0.73 mm/s). The Fe2+ quadrupole splittings were higher at 4.2 K than at room temperature, but the Fe-rich illites again had lower Fe2+ quadrupole splittings both at room temperature (2.69 vs. 2.88 mm/s) and at 4.2 K (2.96 mm/s vs. 3.08 mm/s). Distinction of Fe sites in the illites with cis- and trans-OH coordination was not possible. The presence of tetrahedral Fe3+ was observed only in the most Fe-rich sample (8.4 wt% Fe).