CRITERIA FOR THE INTERCALATION OF SULFURIC-ACID

被引：16

作者：

INAGAKI, M ^{[1
]}

IWASHITA, N ^{[1
]}

HISHIYAMA, Y ^{[1
]}

机构：

[1] MUSASHI INST TECHNOL,SETAGAYA KU,TOKYO 158,JAPAN

来源：

MOLECULAR CRYSTALS AND LIQUID CRYSTALS SCIENCE AND TECHNOLOGY SECTION A-MOLECULAR CRYSTALS AND LIQUID CRYSTALS | 1994年 / 244卷

关键词：

D O I：

10.1080/10587259408050087

中图分类号：

O7 [晶体学];

学科分类号：

0702 ; 070205 ; 0703 ; 080501 ;

摘要：

The criteria for the intercalation of sulfuric acid were studied. The intercalation reaction was found to be governed by the relation between the onset potential values for each stage structure and the upper limit of the saturated potential. It was also shown clearly that the intercalation of sulfuric acid was possible on the hosts with the crystallite thickness along the c-axis above 20 nn and also with positive magnetoresistance at room temperature.

引用

页码：89 / 94

页数：6

共 9 条

[1] THE CHOICE OF OXIDIZERS FOR GRAPHITE HYDROGENOSULFATE CHEMICAL SYNTHESIS [J].

AVDEEV, VV ;

MONYAKINA, LA ;

NIKOLSKAYA, IV ;

SOROKINA, NE ;

SEMENENKO, KN .

CARBON, 1992, 30 (06) :819-823

[2] GRAPHITE-INTERCALATION COMPOUNDS AS POSITIVE ELECTRODES IN GALVANIC CELLS [J].

BECK, F ;

JUNGE, H ;

KROHN, H .

ELECTROCHIMICA ACTA, 1981, 26 (07) :799-809

[3] INFLUENCE OF LATTICE-DEFECTS OF GRAPHITE ON THE FORMATION OF GRAPHITE HYDROGENSULFATE [J].

HORN, D ;

BOEHM, HP .

ZEITSCHRIFT FUR ANORGANISCHE UND ALLGEMEINE CHEMIE, 1979, 456 (09) :117-129

[4] POTENTIAL CHANGE WITH INTERCALATION OF SULFURIC-ACID INTO GRAPHITE BY CHEMICAL OXIDATION [J].

INAGAKI, M ;

IWASHITA, N ;

KOUNO, E .

CARBON, 1990, 28 (01) :49-55

[5] POTENTIAL SURVEY OF INTERCALATION OF SULFURIC-ACID INTO GRAPHITE BY CHEMICAL OXIDATION [J].

IWASHITA, N ;

INAGAKI, M .

SYNTHETIC METALS, 1990, 34 (1-3) :139-144

[6] INTERCALATION OF SULFURIC-ACID INTO GRAPHITE - FOLLOWED BY POTENTIAL MEASUREMENT [J].

IWASHITA, N ;

INAGAKI, M .

NIPPON KAGAKU KAISHI, 1992, (12) :1412-1422

[7]

IWASHITA N, IN PRESS CARBON

[8] RELATIONS BETWEEN CHARGE, POTENTIAL AND FERMI LEVEL DURING ELECTROCHEMICAL INTERCALATION OF H2SO4 INTO PYROGRAPHITE - A 2 CAPACITANCE INTERFACIAL MODEL [J].

METROT, A ;

TIHLI, M .

SYNTHETIC METALS, 1985, 12 (1-2) :517-523

[9] REVERSIBLE ELECTROCHEMICAL INSERTION OF ANIONS IN POLY-PARA-PHENYLENE FROM AQUEOUS-ELECTROLYTES [J].

PRUSS, A ;

BECK, F .

JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 1984, 172 (1-2) :281-288

← 1 →