MEDIAN CRACKING OF BRITTLE SOLIDS DUE TO SCRIBING WITH SHARP INDENTERS

被引:12
作者
CHENG, WL
LING, E
FINNIE, I
机构
[1] Department of Mechanical Engineering, University of California, Berkeley, California
关键词
cracking; indentation; mechanical properties; strain; stress;
D O I
10.1111/j.1151-2916.1990.tb06556.x
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
The process of moving a loaded hard indenter across the surface of a brittle solid to produce a median crack is referred to as “scribing.” As a first step in predicting the depth of median cracking due to sharp indenters, an approximate plastic plane strain analysis is presented for the region under the indenter. This allows the horizontal force transverse to the scribing direction to be predicted. Taking this force and an approximate solution for the stress intensity factor for the crack geometry in scribing leads to a prediction for crack depth as a function of load. The residual stresses which arise on unloading are shown to be a strong function of indenter geometry and may act to extend or partially close the original median crack formed during loading. Reasonable agreement is found between prediction and experiment for six indenter configurations. Copyright © 1990, Wiley Blackwell. All rights reserved
引用
收藏
页码:580 / 586
页数:7
相关论文
共 19 条
[1]  
BANSAL NP, 1988, HDB GLASS PROPERTIES
[2]   THE RESPONSE OF SOLIDS TO ELASTIC PLASTIC INDENTATION .1. STRESSES AND RESIDUAL-STRESSES [J].
CHIANG, SS ;
MARSHALL, DB ;
EVANS, AG .
JOURNAL OF APPLIED PHYSICS, 1982, 53 (01) :298-311
[3]   EFFECT OF ENVIRONMENT ON PENETRATION OF SURFACE DAMAGE AND REMAINING STRENGTH OF AL2O3 [J].
GRUVER, RM ;
KIRCHNER, HP .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1974, 57 (05) :220-223
[4]  
HOLLAND AJ, 1937, J SOC GLASS TECHNOL, V21, P383
[5]   ELASTIC-PLASTIC INDENTATION DAMAGE IN CERAMICS - THE MEDIAN-RADIAL CRACK SYSTEM [J].
LAWN, BR ;
EVANS, AG ;
MARSHALL, DB .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1980, 63 (9-10) :574-581
[6]   EQUILIBRIUM PENNY-LIKE CRACKS IN INDENTATION FRACTURE [J].
LAWN, BR ;
FULLER, ER .
JOURNAL OF MATERIALS SCIENCE, 1975, 10 (12) :2016-2024
[8]   HYSTERESIS IN THE ABRASIVE WEAR OF BRITTLE SOLIDS [J].
MATHIA, T ;
ENCRENAZ, B .
WEAR, 1981, 73 (01) :73-77
[9]   SCRIBING AND SUBSEQUENT FRACTURING OF SILICON SEMICONDUCTOR WAFERS [J].
MISRA, A ;
FINNIE, I .
JOURNAL OF MATERIALS SCIENCE, 1979, 14 (11) :2567-2574
[10]   ELASTIC-PLASTIC INDENTATION - HARDNESS AND FRACTURE [J].
PERROTT, CM .
WEAR, 1977, 45 (03) :293-309